Ca8.5NaAl6O18 |
| |
Nishi F, Takeuchi Y |
 |
Acta Crystallographica B31 (1975) 1169-1173 |
|
The Al6O18 rings of tetrahedra in the structure of Ca8.5NaAl6O18 |
|
_database_code_amcsd 0017813 |
|
10.875 10.859 15.105 90 90 90 Pbca |
|
atom x y z occ B(1,1) B(2,2) B(3,3) B(1,2) B(1,3) B(2,3) |
|
Ca1 .00268 .00196 .51825 .5 .00129 .00103 .00222 .00020 .00007 .00000 |
|
Ca2 -.00394 .01771 .23927 .00204 .00129 .00058 .00036 .00005 -.00002 |
|
Ca3 .00928 .26744 .13313 .00163 .00179 .00054 .00020 -.00012 .00041 |
|
Ca4 .25648 .27066 .25278 .00451 .00131 .00068 .00051 -.00087 .00012 |
|
Ca5 .26267 .24622 .49832 .75 .00256 .00228 .00091 .00002 .00009 -.00006 |
|
Na5 .26267 .24622 .49832 .25 .00256 .00228 .00091 .00002 .00009 -.00006 |
|
Na 0 0 0 .5 .00359 .00928 .00290 -.00388 -.00170 .00456 |
|
Al1 -.00482 -.21407 .11603 .00109 .00093 .00030 -.00021 -.00012 -.00004 |
|
Al2 .23755 -.00327 .11292 .00103 .00142 .00080 -.00035 .00000 .00006 |
|
Al3 .24208 .00543 -.10861 .00084 .00088 .00033 -.00016 -.00004 -.00036 |
|
O1 -.14416 -.13388 .10911 .00265 .00295 .00246 .00138 -.00080 -.00032 |
|
O2 .11066 -.10125 .12634 .00350 .00462 .00164 -.00256 .00079 -.00116 |
|
O3 .28698 -.02208 .00229 .00214 .00274 .00057 -.00071 .00029 .00027 |
|
O4 -.00730 -.28562 .21778 .00794 .00197 .00061 .00061 -.00002 -.00003 |
|
O5 .01956 -.29335 .01724 .00525 .00204 .00060 -.00037 .00034 -.00019 |
|
O6 .35529 -.07220 .17361 .00248 .00216 .00119 .00025 -.00113 -.00039 |
|
O7 .18863 .14794 .13240 .00231 .00267 .00161 .00168 -.00091 -.00029 |
|
O8 .16233 -.12774 -.14188 .00252 .00145 .00139 -.00042 -.00004 -.00069 |
|
O9 .37170 .06610 -.15970 .00228 .00124 .00117 -.00088 .00012 .00030 |
|
|
| Download AMC data (View Text File)
Download CIF data (View Text File)
Download diffraction data (View Text File)
View JMOL 3-D Structure
|
| |
|
Na2CaGe2O6 |
| |
Nishi F, Takeuchi Y |
|
Acta Crystallographica C46 (1990) 544-546 |
|
Structure of sodium calcium germanate Na2CaGe2O6 |
|
_database_code_amcsd 0010123 |
|
10.788 10.788 13.460 90 90 120 R-3m |
|
atom x y z occ Biso |
|
Ge .15040 -.15040 .56698 1.22 |
|
CaM1 0 0 .2473 .35 1.93 |
|
NaM1 0 0 .2473 .65 1.93 |
|
CaM2 .5 0 0 .1 4.03 |
|
NaM2 .5 0 0 .9 4.03 |
|
CaM3 .5 0 .5 .39 2.38 |
|
NaM3 .5 0 .5 .61 2.38 |
|
CaM4 0 0 0 .84 2.41 |
|
NaM4 0 0 0 .16 2.41 |
|
O1 .2783 .0235 .5267 .5 3.0 |
|
O2 .0826 -.1451 .6799 .5 2.0 |
|
O3 .2697 -.2129 .5525 .5 2.7 |
|
|
| Download AMC data (View Text File)
Download CIF data (View Text File)
Download diffraction data (View Text File)
View JMOL 3-D Structure
|
| |
|
Hatrurite |
 |
Nishi F, Takeuchi Y |
 |
Zeitschrift fur Kristallographie 168 (1984) 197-212 |
|
The rhombohedral structure of tricalcium silicate at 1200 C |
|
Locality: synthetic |
|
Sample: T = 1200 C |
|
Note: cannot reconcile reported structure with reported bond lengths |
|
_database_code_amcsd 0010872 |
|
7.135 7.135 25.586 90 90 120 R3m |
|
atom x y z occ Biso B(1,1) B(2,2) B(3,3) B(1,2) B(1,3) B(2,3) |
|
Ca1 .488 -.488 -.001 5.8 .0301 .0301 .0033 .0175 -.0010 .0010 |
|
Ca2 .826 -.826 .111 7.3 .0244 .0244 .0050 .0062 .0014 -.0014 |
|
Ca3 .509 -.509 .225 4.0 .0277 .0277 .0015 .0165 -.0005 .0005 |
|
Si1 0 0 0 2.4 .0099 .0099 .0012 .0050 0 0 |
|
Si2 0 0 .213 5.5 .0157 .0157 .0039 .0079 0 0 |
|
Si3 0 0 .784 3.0 .0087 .0087 .0021 .0044 0 0 |
|
O1 0 0 .385 3 |
|
O2 0 0 .504 13 |
|
O3 0 0 .627 1 |
|
OU14 .057 -.057 .057 1/3 36 |
|
OU15 -.130 .130 .007 1/3 11 |
|
OU16 .223 .148 -.032 1/3 11 |
|
OU24 .016 -.016 .276 .10 1 |
|
OU25 -.128 .128 .199 .10 1 |
|
OU26 .241 .130 .188 .10 1 |
|
OD21 .032 -.032 .152 .23 1 |
|
OD22 -.131 .131 .219 .23 1 |
|
OD23 .234 .137 .241 .23 1 |
|
OU34 -.032 .032 .845 1/3 5 |
|
OU35 .131 -.131 .778 1/3 22 |
|
OU36 .137 .234 .756 1/3 22 |
|
|
| Download AMC data (View Text File)
Download CIF data (View Text File)
Download diffraction data (View Text File)
View JMOL 3-D Structure
|
| |
|
Hatrurite |
|
Nishi F, Takeuchi Y, Maki I |
|
Zeitschrift fur Kristallographie 172 (1985) 297-314 |
|
Tricalcium silicate Ca3O[SiO4]: The monoclinic superstructure |
|
Locality: synthetic |
|
_database_code_amcsd 0010938 |
|
33.083 7.027 18.499 90 94.12 90 Cm |
|
atom x y z occ Biso |
|
Ca1A .0075 0 .0090 .5 4.0 |
|
Ca1B .0024 0 .0056 .5 4.0 |
|
Ca2A .6672 0 .1751 .5 .1 |
|
Ca2B .6673 0 .1741 .5 .1 |
|
Ca3A .3240 0 .3330 .5 1.0 |
|
Ca3B .3193 0 .3307 .5 1.0 |
|
Ca4A .0020 0 .5044 .5 .4 |
|
Ca4B -.0133 0 .4971 .5 .4 |
|
Ca5A .6640 0 .6714 .5 .6 |
|
Ca5B .6632 0 .6697 .5 .6 |
|
Ca6A .3428 0 .8352 .5 1.6 |
|
Ca6B .3301 0 .8213 .5 1.6 |
|
Ca7A .5973 0 -.0611 .5 .2 |
|
Ca7B .5911 0 -.0691 .5 .2 |
|
Ca8A .2611 0 .0952 .5 2.5 |
|
Ca8B .2568 0 .0864 .5 2.5 |
|
Ca9A -.0801 0 .2667 .5 1.3 |
|
Ca9B -.0810 0 .2644 .5 1.3 |
|
Ca10A .5874 0 .4390 .5 .9 |
|
Ca10B .5856 0 .4369 .5 .9 |
|
Ca11A .2575 0 .5989 .5 .2 |
|
Ca11B .2561 0 .5976 .5 .2 |
|
Ca12A -.0742 0 .7698 .5 .6 |
|
Ca12B -.0743 0 .7689 .5 .6 |
|
Ca13A .7356 0 -.1037 .5 .3 |
|
Ca13B .7413 0 -.0957 .5 .3 |
|
Ca14A .4000 0 .0792 .5 3.9 |
|
Ca14B .3982 0 .0706 .5 3.9 |
|
Ca15A .0651 0 .2486 .5 .9 |
|
Ca15B .0628 0 .2445 .5 .9 |
|
Ca16A .7286 0 .4010 .5 1.8 |
|
Ca16B .7272 0 .4042 .5 1.8 |
|
Ca17A .4004 0 .5711 .5 1.4 |
|
Ca17B .3984 0 .5675 .5 1.4 |
|
Ca18A .0694 0 .7491 .5 1.5 |
|
Ca18B .0647 0 .7349 .5 1.5 |
|
Ca19A -.0846 .2988 -.0926 .5 1.0 |
|
Ca19B -.0793 .2677 -.0789 .5 1.0 |
|
Ca20A .5799 .3018 .0844 .5 1.6 |
|
Ca20B .5850 .2058 .1013 .5 1.6 |
|
Ca21A .2411 .2447 .2470 .5 .2 |
|
Ca21B .2459 .2559 .2501 .5 .2 |
|
Ca22A -.0941 .2566 .4130 .5 .2 |
|
Ca22B -.0885 .2550 .4273 .5 .2 |
|
Ca23A .5744 .2726 .5851 .5 .8 |
|
Ca23B .5784 .2399 .5943 .5 .8 |
|
Ca24A .2435 .2491 .7443 .5 .5 |
|
Ca24B .2468 .2347 .7554 .5 .5 |
|
Ca25A .0052 .2343 -.1598 .5 .1 |
|
Ca25B .0051 .2338 -.1501 .5 .1 |
|
Ca26A .6704 .2318 .0073 .5 .2 |
|
Ca26B .6771 .2306 .0144 .5 .2 |
|
Ca27A .3354 .2257 .1731 .5 .3 |
|
Ca27B .3365 .2385 .1853 .5 .3 |
|
Ca28A -.0047 .2281 .3417 .5 .2 |
|
Ca28B .0018 .2540 .3490 .5 .2 |
|
Ca29A .6630 .2288 .5097 .5 .9 |
|
Ca29B .6688 .2292 .5147 .5 .9 |
|
Ca30A .3350 .2592 .6750 .5 .7 |
|
Ca30B .3360 .2165 .6827 .5 .7 |
|
Ca31A .8294 .2577 -.0192 .5 1.2 |
|
Ca31B .8306 .2893 -.0026 .5 1.2 |
|
Ca32A .4840 .2722 .1583 .5 1.8 |
|
Ca32B .4905 .2303 .1584 .5 1.8 |
|
Ca33A .1468 .2503 .3304 .5 1.4 |
|
Ca33B .1562 .2900 .3320 .5 1.4 |
|
Ca34A .8167 .2762 .4875 .5 .6 |
|
Ca34B .8224 .2520 .4918 .5 .6 |
|
Ca35A .4941 .2854 .6505 .5 .9 |
|
Ca35B .4893 .2759 .6649 .5 .9 |
|
Ca36A .1569 .2749 .8198 .5 .1 |
|
Ca36B .1643 .2675 .8283 .5 .1 |
|
Si1 .0833 0 .4288 2.1 |
|
Si2 .2384 0 -.0838 .3 |
|
Si3 .4292 0 .7460 1.5 |
|
Si4 .5699 0 .7506 .2 |
|
Si5 -.0943 0 .0741 .1 |
|
Si6 -.1015 0 .5918 1.5 |
|
Si7 .0966 0 -.0851 .5 |
|
Si8 .1637 0 .1591 1.0 |
|
Si9 .1628 0 .6629 .3 |
|
Si10 .2340 0 .4118 3.8 |
|
Si11 .4214 0 .2509 1.5 |
|
Si12 .5008 0 .0039 .7 |
|
Si13 .4975 0 .5004 2.5 |
|
Si14 .5682 0 .2442 .3 |
|
Si15 .7600 0 .0882 .2 |
|
Si16 .7563 0 .5803 .2 |
|
Si17 -.1748 0 .3338 .4 |
|
Si18 -.1693 0 -.1575 .2 |
|
O1A .990 0 .245 .5 4.2 |
|
O1B .988 0 .245 .5 4.2 |
|
O2A .038 0 .119 .5 3.8 |
|
O2B .052 0 .124 .5 3.8 |
|
O3A .030 0 .599 .5 2.8 |
|
O3B .038 0 .610 .5 2.8 |
|
O4A -.004 0 .753 .5 1.0 |
|
O4B -.005 0 .754 .5 1.0 |
|
O5A .372 0 -.077 .5 2.8 |
|
O5B .373 0 -.047 .5 2.8 |
|
O6A .329 0 .075 .5 4.1 |
|
O6B .331 0 .077 .5 4.1 |
|
O7A .289 0 .211 .5 2.7 |
|
O7B .289 0 .223 .5 2.7 |
|
O8A .362 0 .441 .5 .8 |
|
O8B .362 0 .442 .5 .8 |
|
O9A .325 0 .583 .5 .1 |
|
O9B .334 0 .595 .5 .1 |
|
O10A .282 0 .724 .5 1.4 |
|
O10B .293 0 .732 .5 1.4 |
|
O11A .666 0 -.093 .5 .5 |
|
O11B .675 0 -.081 .5 .5 |
|
O12A .627 0 .049 .5 1.5 |
|
O12B .634 0 .067 .5 1.5 |
|
O13A .706 0 .285 .5 2.6 |
|
O13B .704 0 .290 .5 2.6 |
|
O14A .648 0 .421 .5 2.1 |
|
O14B .655 0 .414 .5 2.1 |
|
O15A .608 0 .564 .5 1.5 |
|
O15B .622 0 .567 .5 1.5 |
|
O16A .705 0 .763 .5 1.4 |
|
O16B .709 0 .771 .5 1.4 |
|
O17A .949 0 .376 .5 1.5 |
|
O17B .957 0 .401 .5 1.5 |
|
O18A .960 0 .897 .5 .8 |
|
O18B .965 0 .907 .5 .8 |
|
OD11 .111 0 .357 8.1 |
|
OD12 .035 0 .408 4.2 |
|
OD13 .096 .187 .474 3.2 |
|
OU24 .215 0 -.011 .5 |
|
OU25 .286 0 -.063 2.9 |
|
OU26 .226 .184 -.133 2.1 |
|
OD31 .450 0 .668 1.7 |
|
OD32 .379 0 .730 2.3 |
|
OD33 .443 .183 .791 1.6 |
|
OU44 .549 0 .830 2.1 |
|
OU45 .616 0 .767 1.5 |
|
OU46 .555 .188 .704 2.0 |
|
OU54 -.118 0 .149 1.5 |
|
OU55 -.044 0 .093 1.2 |
|
OU56 -.107 .187 .027 2.7 |
|
OU64 -.123 0 .669 4.7 |
|
OU65 -.054 0 .608 3.8 |
|
OU66 -.117 .186 .542 2.3 |
|
OD71 .119 0 -.161 .68 .7 |
|
OD72 .048 0 -.103 .68 1.6 |
|
OD73 .110 .189 -.038 .68 3.9 |
|
OU74 .074 0 -.009 .32 4.0 |
|
OU75 .055 0 -.138 .32 2.0 |
|
OU76 .125 .189 -.073 .32 1.9 |
|
OG81 .141 .050 .080 .5 3.5 |
|
OG82 .134 -.123 .208 .5 3.5 |
|
OG83 .205 -.123 .151 .5 3.5 |
|
OG84 .176 .197 .202 .5 3.5 |
|
OD91 .185 0 .587 .59 1.3 |
|
OD92 .114 0 .645 .59 1.3 |
|
OD93 .176 .189 .710 .59 1.3 |
|
OU94 .140 0 .739 .32 1.3 |
|
OU95 .212 0 .681 .32 1.3 |
|
OU96 .141 .189 .627 .32 1.3 |
|
OG91 .140 .050 .584 .045 1.3 |
|
OG92 .133 -.123 .712 .045 1.3 |
|
OG93 .204 -.123 .655 .045 1.3 |
|
OG94 .175 .197 .706 .045 1.3 |
|
OD101 .255 0 .335 .59 11.0 |
|
OD102 .268 0 .480 .59 2.7 |
|
OD103 .206 .189 .415 .59 2. |
|
OU104 .212 0 .487 .41 6. |
|
OU105 .283 0 .430 .41 2. |
|
OU106 .221 .189 .365 .41 3. |
|
OD111 .444 0 .175 .57 5. |
|
OD112 .372 0 .233 .57 3. |
|
OD113 .435 .189 .298 .57 3. |
|
OU114 .399 0 .327 .43 5. |
|
OU115 .382 0 .193 .43 5. |
|
OU116 .450 .189 .257 .43 2.3 |
|
OU124 .478 0 .080 .43 6. |
|
OU125 .550 0 .022 .43 6. |
|
OU126 .487 .189 -.043 .43 6. |
|
OG121 .478 .050 -.075 .285 6. |
|
OG122 .466 -.123 .040 .285 6. |
|
OG123 .542 -.123 -.004 .285 6. |
|
OG124 .513 .197 .047 .285 6. |
|
OD131 .520 0 .425 .37 3.4 |
|
OD132 .448 0 .483 .37 3.4 |
|
OD133 .511 .189 .547 .37 3.4 |
|
OG131 .520 .050 .580 .315 3.4 |
|
OG132 .526 -.128 .451 .315 3.4 |
|
OG133 .456 -.123 .508 .315 3.4 |
|
OG134 .481 .197 .463 .315 3.4 |
|
OD141 .591 0 .169 .37 16. |
|
OD142 .602 0 .312 .37 12. |
|
OD143 .540 .189 .248 .37 2.4 |
|
OU144 .546 0 .320 .63 12. |
|
OU145 .617 0 .262 .63 6. |
|
OU146 .555 .189 .197 .63 16. |
|
OD151 .782 0 .013 .22 11. |
|
OD152 .711 0 .070 .22 4. |
|
OD153 .773 .189 .135 .22 2. |
|
OU154 .738 0 .164 .78 6. |
|
OU155 .726 0 .020 .78 2.4 |
|
OU156 .788 .189 .085 .78 3.3 |
|
OD161 .778 0 .505 .93 0.4 |
|
OD162 .707 0 .565 .93 0.5 |
|
OD163 .769 .191 .626 .93 1.4 |
|
OU164 .734 0 .656 .07 0.8 |
|
OU165 .717 0 .522 .07 0.8 |
|
OU166 .787 .180 .594 .07 0.8 |
|
OU174 -.197 0 .409 .07 4.6 |
|
OU175 -.126 0 .352 .07 4.6 |
|
OU176 -.188 .189 .287 .07 4.6 |
|
OG171 -.197 .050 .255 .2325 4.6 |
|
OG172 -.204 -.123 .383 .2325 4.6 |
|
OG173 -.134 -.123 .326 .2325 4.6 |
|
OG174 -.163 .197 .377 .2325 4.6 |
|
OG175 -.152 .050 .413 .2325 4.6 |
|
OG176 -.145 -.123 .285 .2325 4.6 |
|
OG177 -.216 -.123 .342 .2325 4.6 |
|
OG178 -.187 .197 .291 .2325 4.6 |
|
OU184 -.192 0 -.082 .78 2.0 |
|
OU185 -.120 0 -.140 .78 2.0 |
|
OU186 -.183 .189 -.204 .78 2.0 |
|
OG181 -.192 .050 -.237 .11 2.0 |
|
OG182 -.199 -.123 -.108 .11 2.0 |
|
OG183 -.128 -.123 -.165 .11 2.0 |
|
OG184 -.158 .210 -.125 .11 2.0 |
|
|
| Download AMC data (View Text File)
Download CIF data (View Text File)
Download diffraction data (View Text File)
View JMOL 3-D Structure
|
| |
Multiple datasets can be concatenated into a single downloadable file by
selecting the datasets and then hitting the "Download Selected Data" button.