Parkerite Fleet M E American Mineralogist 58 (1973) 435-439 The crystal structure of parkerite (Ni3Bi2S2) _database_code_amcsd 0000318 CELL PARAMETERS: 5.5450 5.7310 4.0520 90.000 90.000 90.000 SPACE GROUP: Pmam X-RAY WAVELENGTH: 1.541838 Cell Volume: 128.766 Density (g/cm3): 8.486 MAX. ABS. INTENSITY / VOLUME**2: 227.1785400 RIR: 8.716 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.46 14.80 5.7310 0 1 0 2 21.94 28.43 4.0520 0 0 1 2 22.31 55.68 3.9850 1 1 0 4 26.95 7.75 3.3086 0 1 1 4 31.21 23.77 2.8655 0 2 0 2 31.49 100.00 2.8412 1 1 1 8 32.29 23.05 2.7725 2 0 0 2 35.26 1.11 2.5457 1 2 0 4 35.98 3.72 2.4958 2 1 0 4 38.48 49.83 2.3396 0 2 1 4 39.38 48.82 2.2881 2 0 1 4 41.91 1.67 2.1556 1 2 1 8 42.54 4.24 2.1250 2 1 1 8 44.73 23.55 2.0260 0 0 2 2 45.52 42.86 1.9925 2 2 0 4 47.61 1.38 1.9102 0 1 2 4 50.53 7.75 1.8062 1 3 0 4 50.54 13.98 1.8060 1 1 2 8 51.08 12.32 1.7880 2 2 1 8 51.98 6.44 1.7591 3 1 0 4 55.55 8.12 1.6543 0 2 2 4 55.72 18.65 1.6497 1 3 1 8 56.24 8.30 1.6358 2 0 2 4 57.08 15.95 1.6136 3 1 1 8 58.69 1.50 1.5730 2 1 2 8 63.43 1.22 1.4664 2 3 1 8 65.10 5.70 1.4327 0 4 0 2 65.73 24.55 1.4206 2 2 2 8 67.58 5.78 1.3863 4 0 0 2 69.60 1.97 1.3508 0 4 1 4 69.61 1.32 1.3507 0 0 3 2 69.75 5.82 1.3482 1 3 2 8 70.95 2.76 1.3283 3 3 0 4 70.96 5.04 1.3283 3 1 2 8 72.00 2.39 1.3116 4 0 1 4 74.12 6.60 1.2792 1 1 3 8 74.55 2.53 1.2728 2 4 0 4 75.29 6.74 1.2623 3 3 1 8 76.31 2.80 1.2479 4 2 0 4 78.25 5.37 1.2217 0 2 3 4 78.82 9.35 1.2143 2 4 1 8 78.82 5.47 1.2142 2 0 3 4 80.54 9.86 1.1926 4 2 1 8 82.45 5.18 1.1698 0 4 2 4 84.73 5.51 1.1441 4 0 2 4 86.76 1.82 1.1225 1 5 0 4 87.19 2.69 1.1180 2 2 3 8 87.89 3.11 1.1109 3 3 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.