Diopside Cameron M, Sueno S, Prewitt C T, Papike J J American Mineralogist 58 (1973) 594-618 High-temperature crystal chemistry of acmite, diopside, hedenbergite, jadeite, spodumene, and ureyite T = 400 C pyroxene _database_code_amcsd 0000341 CELL PARAMETERS: 9.7760 8.9790 5.2670 90.000 105.940 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 444.554 Density (g/cm3): 3.235 MAX. ABS. INTENSITY / VOLUME**2: 11.56985871 RIR: 1.165 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.78 3.25 4.4895 0 2 0 2 24.25 2.60 3.6700 1 1 1 4 26.53 11.06 3.3595 0 2 1 4 27.47 25.83 3.2464 2 2 0 4 29.74 100.00 3.0043 -2 2 1 4 30.21 26.70 2.9584 3 1 0 4 30.80 35.21 2.9033 -3 1 1 4 31.37 1.15 2.8519 1 3 0 4 34.79 23.37 2.5786 -1 3 1 4 35.35 2.04 2.5394 -2 0 2 2 35.45 40.24 2.5322 0 0 2 2 35.57 39.51 2.5242 2 2 1 4 37.46 1.08 2.4009 1 3 1 4 39.04 16.35 2.3072 3 1 1 4 40.62 9.09 2.2209 1 1 2 4 40.83 1.34 2.2103 -2 2 2 4 40.92 8.99 2.2056 0 2 2 4 41.73 8.98 2.1643 3 3 0 4 42.18 17.29 2.1425 -3 3 1 4 42.75 8.07 2.1151 -4 2 1 4 43.46 1.02 2.0820 4 2 0 4 44.13 18.23 2.0522 0 4 1 4 44.84 10.99 2.0214 -4 0 2 2 45.09 6.53 2.0106 2 0 2 2 45.90 6.86 1.9771 -1 3 2 4 48.79 2.06 1.8664 3 3 1 4 49.54 6.26 1.8401 5 1 0 4 49.68 2.80 1.8350 2 2 2 4 50.13 3.32 1.8198 1 3 2 4 51.83 12.84 1.7639 1 5 0 4 53.08 1.69 1.7254 -5 1 2 4 54.17 1.14 1.6931 -1 5 1 4 54.64 4.39 1.6798 0 4 2 4 55.21 5.80 1.6636 -3 1 3 4 56.41 13.31 1.6311 -5 3 1 4 56.47 15.66 1.6296 -2 2 3 4 56.71 4.65 1.6232 4 4 0 4 57.93 1.65 1.5920 5 3 0 4 58.95 3.29 1.5667 6 0 0 2 59.31 4.07 1.5581 3 5 0 4 60.33 4.48 1.5341 -6 0 2 2 60.48 2.06 1.5307 -6 2 1 4 60.68 5.73 1.5262 4 0 2 2 61.13 1.20 1.5160 -5 3 2 4 61.45 11.84 1.5089 -1 3 3 4 61.96 1.60 1.4977 2 4 2 4 62.01 4.24 1.4965 0 6 0 2 63.40 1.45 1.4670 4 4 1 4 64.15 2.23 1.4517 -6 2 2 4 64.49 1.26 1.4450 4 2 2 4 64.98 1.83 1.4352 0 6 1 4 65.41 16.02 1.4268 5 3 1 4 65.97 8.26 1.4161 -3 5 2 4 66.10 3.79 1.4136 1 5 2 4 67.18 3.91 1.3935 2 2 3 4 67.93 1.09 1.3799 -7 1 1 4 67.94 1.03 1.3796 -2 4 3 4 69.69 1.39 1.3492 0 4 3 4 70.56 5.91 1.3347 -7 1 2 4 70.84 3.55 1.3301 6 2 1 4 70.97 1.09 1.3281 7 1 0 4 71.36 2.96 1.3218 -5 3 3 4 73.30 3.34 1.2914 -3 1 4 4 73.43 1.79 1.2895 -1 1 4 4 73.45 3.08 1.2893 -2 6 2 4 73.51 5.55 1.2883 0 6 2 4 74.77 1.46 1.2697 -4 0 4 2 75.02 2.97 1.2661 0 0 4 2 75.06 1.35 1.2655 -7 3 1 4 75.95 6.33 1.2528 3 5 2 4 76.61 1.13 1.2437 -1 7 1 4 78.22 1.72 1.2220 1 7 1 4 82.01 1.43 1.1750 8 0 0 2 84.07 2.71 1.1514 -6 0 4 2 87.94 1.36 1.1104 2 2 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.