Liebenbergite Lager G A, Meagher E P American Mineralogist 63 (1978) 365-377 High-temperature structural study of six olivines T = 300 deg C, synthetic Ni2SiO4 _database_code_amcsd 0000643 CELL PARAMETERS: 4.7440 10.1510 5.9330 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 285.712 Density (g/cm3): 4.869 MAX. ABS. INTENSITY / VOLUME**2: 26.47885077 RIR: 1.771 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.47 6.99 5.0755 0 2 0 2 20.67 20.43 4.2978 1 1 0 4 23.06 7.40 3.8568 0 2 1 4 24.02 5.09 3.7052 1 0 1 4 25.59 77.73 3.4806 1 1 1 8 25.70 4.23 3.4658 1 2 0 4 29.86 2.31 2.9926 1 2 1 8 30.13 4.93 2.9665 0 0 2 2 32.50 84.34 2.7547 1 3 0 4 35.04 44.38 2.5611 0 2 2 4 35.37 15.61 2.5378 0 4 0 2 35.94 73.47 2.4986 1 3 1 8 36.81 100.00 2.4414 1 1 2 8 37.93 19.06 2.3720 2 0 0 2 38.59 11.10 2.3333 0 4 1 4 38.99 3.62 2.3098 2 1 0 4 40.01 11.68 2.2537 1 2 2 8 40.30 8.54 2.2377 1 4 0 4 41.97 5.67 2.1524 2 1 1 8 44.86 1.04 2.0205 2 2 1 8 44.90 8.34 2.0186 1 3 2 8 47.13 1.51 1.9284 0 4 2 4 48.79 4.04 1.8665 1 5 0 4 50.82 11.72 1.7966 1 1 3 8 51.32 8.38 1.7804 1 5 1 8 52.59 77.34 1.7403 2 2 2 8 52.83 28.44 1.7329 2 4 0 4 53.33 1.37 1.7177 1 2 3 8 55.22 9.70 1.6634 2 4 1 8 56.57 9.17 1.6270 0 6 1 4 57.35 16.78 1.6065 1 3 3 8 58.42 17.50 1.5798 1 5 2 8 59.13 4.30 1.5625 3 1 0 4 59.23 5.29 1.5599 0 4 3 4 61.36 6.89 1.5110 3 1 1 8 61.75 1.10 1.5022 2 1 3 8 62.02 2.06 1.4963 2 4 2 8 62.19 1.84 1.4928 2 5 1 8 62.63 20.06 1.4833 0 0 4 2 63.28 27.95 1.4696 0 6 2 4 65.11 6.39 1.4326 3 3 0 4 66.71 1.42 1.4021 1 1 4 8 67.23 8.17 1.3926 3 3 1 8 67.55 13.38 1.3868 1 7 0 4 67.79 10.03 1.3824 3 1 2 8 69.21 2.47 1.3574 1 5 3 8 69.91 5.51 1.3455 3 2 2 8 70.12 1.70 1.3421 3 4 0 4 70.14 2.58 1.3417 2 6 1 8 72.16 1.54 1.3090 3 4 1 8 72.36 11.86 1.3060 1 3 4 8 72.53 2.02 1.3033 2 4 3 8 73.69 3.26 1.2856 0 6 3 4 74.03 3.49 1.2806 0 4 4 4 74.83 1.19 1.2689 0 8 0 2 75.61 6.08 1.2576 2 0 4 4 76.21 6.97 1.2493 2 6 2 8 77.92 2.25 1.2260 3 1 3 8 78.32 1.12 1.2208 3 5 1 8 81.09 4.90 1.1860 4 0 0 2 83.19 1.52 1.1612 1 5 4 8 83.28 3.95 1.1602 3 3 3 8 84.19 7.74 1.1500 3 5 2 8 84.75 1.53 1.1438 1 1 5 8 86.01 1.54 1.1303 2 6 3 8 86.34 9.08 1.1268 2 4 4 8 87.11 3.54 1.1188 2 8 0 4 87.93 1.28 1.1105 3 4 3 8 89.04 1.65 1.0995 2 8 1 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.