Zn(Zn.1Li.6Si.3)SiO4-alpha Yu S C, Smith D K, Austerman S B American Mineralogist 63 (1978) 1241-1248 The crystal structures and the phase transformation of Zn-Li silicates T = room temperature _database_code_amcsd 0000692 CELL PARAMETERS: 6.3400 10.5160 5.0110 90.000 90.500 90.000 SPACE GROUP: P2_1/n X-RAY WAVELENGTH: 1.541838 Cell Volume: 334.078 Density (g/cm3): 3.511 MAX. ABS. INTENSITY / VOLUME**2: 10.17995150 RIR: 0.944 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 16.33 59.38 5.4294 1 1 0 4 16.86 18.07 5.2580 0 2 0 2 19.62 3.56 4.5235 0 1 1 4 21.96 67.00 4.0472 1 2 0 4 22.52 67.14 3.9480 -1 0 1 2 22.72 9.24 3.9146 1 0 1 2 24.08 29.03 3.6961 -1 1 1 4 24.26 94.92 3.6686 1 1 1 4 24.54 58.46 3.6274 0 2 1 4 28.15 34.64 3.1699 2 0 0 2 28.43 14.02 3.1399 1 2 1 4 29.11 57.47 3.0676 1 3 0 4 31.14 24.87 2.8723 0 3 1 4 33.00 100.00 2.7147 2 2 0 4 34.10 68.76 2.6290 0 4 0 2 34.21 7.59 2.6212 -1 3 1 4 34.34 8.52 2.6114 1 3 1 4 34.42 17.75 2.6056 -2 1 1 4 34.68 17.64 2.5864 2 1 1 4 35.84 90.83 2.5054 0 0 2 2 36.88 20.38 2.4372 0 1 2 4 37.02 1.41 2.4285 1 4 0 4 37.56 24.12 2.3944 -2 2 1 4 37.81 27.51 2.3795 2 2 1 4 38.68 13.31 2.3280 0 4 1 4 39.50 2.02 2.2814 -1 1 2 4 39.73 5.16 2.2684 1 1 2 4 39.86 2.99 2.2618 0 2 2 4 41.26 2.88 2.1882 -1 4 1 4 42.32 1.47 2.1356 -1 2 2 4 42.36 15.48 2.1338 -2 3 1 4 42.54 15.55 2.1250 1 2 2 4 42.58 14.50 2.1232 2 3 1 4 43.69 4.33 2.0718 3 1 0 4 44.45 1.58 2.0383 0 3 2 4 44.79 11.24 2.0236 2 4 0 4 45.44 3.35 1.9962 1 5 0 4 45.98 6.17 1.9740 -2 0 2 2 46.39 6.34 1.9573 2 0 2 2 46.71 7.22 1.9445 -1 3 2 4 46.80 2.21 1.9411 3 0 1 2 46.83 7.71 1.9401 -2 1 2 4 46.85 5.78 1.9393 0 5 1 4 46.92 8.70 1.9365 1 3 2 4 47.24 6.25 1.9242 2 1 2 4 47.34 16.91 1.9204 -3 1 1 4 47.64 2.98 1.9089 3 1 1 4 48.42 9.83 1.8800 -2 4 1 4 48.62 10.02 1.8727 2 4 1 4 49.08 13.24 1.8562 -1 5 1 4 49.18 5.06 1.8527 1 5 1 4 49.31 12.93 1.8480 -2 2 2 4 49.70 12.95 1.8343 2 2 2 4 49.80 5.20 1.8310 -3 2 1 4 50.09 1.21 1.8210 3 2 1 4 50.31 16.48 1.8137 0 4 2 4 50.42 11.69 1.8098 3 3 0 4 52.19 7.48 1.7527 0 6 0 2 52.38 3.51 1.7467 -1 4 2 4 52.57 3.28 1.7408 1 4 2 4 53.72 2.07 1.7063 -3 3 1 4 54.00 1.49 1.6981 3 3 1 4 54.30 1.92 1.6893 1 6 0 4 55.72 2.52 1.6496 0 1 3 4 55.82 2.91 1.6471 3 4 0 4 56.88 8.17 1.6186 -1 0 3 2 57.19 3.06 1.6109 0 5 2 4 57.62 3.42 1.5997 1 6 1 4 57.88 3.98 1.5931 1 1 3 4 58.01 1.73 1.5900 3 1 2 4 58.21 30.00 1.5849 4 0 0 2 58.47 3.22 1.5785 -2 4 2 4 58.82 3.37 1.5700 2 4 2 4 59.27 1.35 1.5592 1 5 2 4 59.64 2.07 1.5502 -3 2 2 4 60.04 2.87 1.5409 1 2 3 4 60.16 2.23 1.5381 3 2 2 4 60.35 51.50 1.5338 2 6 0 4 61.50 16.60 1.5078 0 3 3 4 62.28 1.49 1.4907 3 5 0 4 63.15 1.46 1.4723 -3 3 2 4 63.28 3.53 1.4695 -1 3 3 4 63.33 10.63 1.4685 -2 1 3 4 63.53 3.68 1.4643 1 3 3 4 63.65 4.86 1.4619 3 3 2 4 63.66 1.55 1.4618 1 7 0 4 63.83 10.22 1.4582 2 1 3 4 63.95 5.12 1.4557 -4 2 1 4 64.29 5.19 1.4490 4 2 1 4 64.77 6.30 1.4393 -2 5 2 4 64.79 2.46 1.4390 0 7 1 4 64.93 4.64 1.4361 0 6 2 4 65.10 5.09 1.4328 2 5 2 4 65.18 2.47 1.4312 -3 5 1 4 65.43 3.52 1.4264 3 5 1 4 65.87 1.28 1.4179 2 2 3 4 66.61 4.91 1.4041 -1 7 1 4 66.69 1.19 1.4026 1 7 1 4 67.33 1.76 1.3906 -4 3 1 4 67.66 1.38 1.3848 4 3 1 4 68.02 1.94 1.3783 -1 4 3 4 68.37 3.11 1.3720 3 4 2 4 68.73 15.14 1.3658 -2 3 3 4 69.21 14.70 1.3575 2 3 3 4 69.22 9.85 1.3574 4 4 0 4 69.96 6.64 1.3447 -4 0 2 2 70.60 7.01 1.3342 4 0 2 2 70.61 4.19 1.3339 -4 1 2 4 71.25 2.92 1.3236 4 1 2 4 71.81 1.20 1.3145 0 8 0 2 71.93 3.59 1.3126 -4 4 1 4 72.06 12.18 1.3106 -2 6 2 4 72.23 5.43 1.3080 0 5 3 4 72.25 4.22 1.3077 4 4 1 4 72.37 3.21 1.3058 -3 1 3 4 72.37 12.39 1.3057 2 6 2 4 72.43 2.42 1.3049 3 0 3 2 72.45 3.97 1.3045 -3 6 1 4 73.50 1.33 1.2884 0 7 2 4 73.59 1.61 1.2871 1 8 0 4 73.88 2.08 1.2827 -1 5 3 4 74.30 1.75 1.2766 -3 2 3 4 74.65 5.78 1.2715 0 8 1 4 76.60 5.00 1.2439 0 1 4 4 77.43 2.11 1.2326 5 2 0 4 77.47 2.09 1.2320 -3 3 3 4 77.49 2.18 1.2318 -5 0 1 2 78.16 1.67 1.2229 3 3 3 4 78.50 1.91 1.2184 5 1 1 4 80.06 3.07 1.1986 -1 2 4 4 80.17 2.37 1.1972 -4 4 2 4 80.31 1.38 1.1955 -2 7 2 4 80.57 2.62 1.1923 5 3 0 4 80.62 1.12 1.1917 2 7 2 4 80.78 2.51 1.1897 4 4 2 4 80.92 2.15 1.1880 3 7 1 4 81.06 3.40 1.1864 1 6 3 4 81.50 1.05 1.1810 -2 8 1 4 81.62 1.23 1.1796 0 3 4 4 81.65 1.08 1.1792 2 8 1 4 81.96 1.87 1.1756 4 6 0 4 83.18 1.30 1.1614 -2 1 4 4 83.78 1.19 1.1545 2 1 4 4 84.27 2.07 1.1491 1 9 0 4 84.58 2.00 1.1457 -1 8 2 4 85.29 1.55 1.1379 0 9 1 4 85.76 1.27 1.1330 -4 5 2 4 87.29 4.62 1.1170 0 7 3 4 87.37 2.08 1.1162 3 8 0 4 87.80 2.43 1.1118 1 4 4 4 88.75 2.08 1.1023 5 2 2 4 88.87 1.27 1.1011 -1 7 3 4 89.32 3.71 1.0968 -4 3 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.