Zn(Zn.1Li.6Si.3)SiO4-beta Yu S C, Smith D K, Austerman S B American Mineralogist 63 (1978) 1241-1248 The crystal structures and the phase transformation of Zn-Li silicates T = 450 C _database_code_amcsd 0000693 CELL PARAMETERS: 6.4060 10.5200 5.0430 90.000 90.000 90.000 SPACE GROUP: Pmnb X-RAY WAVELENGTH: 1.541838 Cell Volume: 339.853 Density (g/cm3): 2.547 MAX. ABS. INTENSITY / VOLUME**2: 6.913649143 RIR: 0.884 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 21.86 100.00 4.0652 1 2 0 4 22.44 91.91 3.9625 1 0 1 4 24.00 13.69 3.7082 1 1 1 8 28.20 15.84 3.1649 1 2 1 8 31.06 7.64 2.8790 0 3 1 4 32.74 68.94 2.7357 2 2 0 4 34.09 48.02 2.6300 0 4 0 2 34.14 21.24 2.6260 1 3 1 8 34.24 27.45 2.6186 2 1 1 8 35.61 63.15 2.5215 0 0 2 2 36.65 2.15 2.4520 0 1 2 4 36.95 1.58 2.4329 1 4 0 4 37.40 2.17 2.4047 2 2 1 8 41.20 2.20 2.1913 1 4 1 8 42.17 5.11 2.1428 1 2 2 8 42.21 13.40 2.1412 2 3 1 8 44.24 1.22 2.0472 0 3 2 4 46.78 4.90 1.9418 0 5 1 4 47.01 4.05 1.9329 3 1 1 8 49.14 16.52 1.8541 2 2 2 8 49.49 7.61 1.8418 3 2 1 8 50.12 9.82 1.8201 0 4 2 4 53.09 1.09 1.7250 2 3 2 8 53.42 4.62 1.7151 3 3 1 8 54.24 2.81 1.6911 1 6 0 4 55.33 1.26 1.6605 2 5 1 8 55.43 4.01 1.6577 3 4 0 4 56.61 3.43 1.6260 1 0 3 4 57.34 2.50 1.6069 1 1 3 8 57.48 2.10 1.6034 1 6 1 8 57.55 17.35 1.6015 4 0 0 2 58.31 1.42 1.5825 2 4 2 8 60.17 29.06 1.5380 2 6 0 4 61.14 4.78 1.5158 0 3 3 4 63.02 8.81 1.4751 1 3 3 8 63.08 13.13 1.4738 2 1 3 8 64.62 2.58 1.4424 2 5 2 8 64.72 1.32 1.4403 0 7 1 4 67.63 1.05 1.3852 3 4 2 8 68.48 11.10 1.3701 2 3 3 8 68.61 5.36 1.3679 4 4 0 4 69.54 7.11 1.3519 4 0 2 4 70.19 1.74 1.3408 4 1 2 8 71.46 1.60 1.3202 4 4 1 8 71.89 3.87 1.3133 0 5 3 4 71.91 12.77 1.3130 2 6 2 8 72.07 3.17 1.3105 3 1 3 8 72.19 4.66 1.3086 3 6 1 8 73.52 1.93 1.2881 1 8 0 4 73.63 1.05 1.2866 1 5 3 8 74.58 1.32 1.2725 0 8 1 4 76.03 1.08 1.2518 0 1 4 4 76.53 2.89 1.2448 5 2 0 4 76.75 2.85 1.2418 5 0 1 4 77.17 4.50 1.2361 3 3 3 8 77.21 1.30 1.2355 4 5 1 8 79.76 2.26 1.2023 4 4 2 8 81.05 1.14 1.1864 0 3 4 4 86.96 2.27 1.1204 0 7 3 4 87.02 2.50 1.1197 3 8 0 4 87.37 1.26 1.1162 5 2 2 8 87.73 1.49 1.1125 2 3 4 8 88.62 1.22 1.1036 1 7 3 8 88.90 1.36 1.1009 4 3 3 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.