Zircon Hazen R M, Finger L W American Mineralogist 64 (1979) 196-201 Crystal structure and compressibility of zircon at high pressure crystal No. 1, P = 28.9 kbar _database_code_amcsd 0000701 CELL PARAMETERS: 6.5737 6.5737 5.9638 90.000 90.000 90.000 SPACE GROUP: I4_1/amd X-RAY WAVELENGTH: 1.541838 Cell Volume: 257.717 Density (g/cm3): 4.724 MAX. ABS. INTENSITY / VOLUME**2: 74.72072683 RIR: 5.151 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 20.10 42.98 4.4170 1 0 1 8 27.13 100.00 3.2868 2 0 0 4 34.00 7.71 2.6369 2 1 1 16 35.78 58.39 2.5099 1 1 2 8 38.74 12.73 2.3242 2 2 0 4 40.86 6.16 2.2085 2 0 2 8 44.03 20.40 2.0568 3 0 1 8 47.80 13.68 1.9028 1 0 3 8 52.48 14.30 1.7436 3 2 1 16 53.75 53.98 1.7053 3 1 2 16 55.83 3.59 1.6468 2 1 3 16 55.95 14.93 1.6434 4 0 0 4 60.07 2.81 1.5403 4 1 1 16 62.27 3.05 1.4909 0 0 4 2 63.15 2.93 1.4723 3 0 3 8 63.26 9.76 1.4699 4 2 0 8 68.21 16.85 1.3749 3 3 2 8 69.19 10.19 1.3578 2 0 4 8 73.80 5.20 1.2839 4 3 1 16 75.80 8.82 1.2549 2 2 4 8 76.61 2.60 1.2438 4 1 3 16 81.31 9.57 1.1833 5 1 2 16 83.12 2.97 1.1621 4 4 0 4 88.45 2.66 1.1053 2 1 5 16 88.56 5.10 1.1042 4 0 4 8 89.34 2.02 1.0966 5 0 3 8 89.44 4.58 1.0956 6 0 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.