Ni2SiO4 Finger L W, Hazen R M, Yagi T American Mineralogist 64 (1979) 1002-1009 Crystal structures and electron densities of nickel and iron silicate spinels at elevated temperature or pressure P = 22.5 kbar, T = 23 C _database_code_amcsd 0000744 CELL PARAMETERS: 8.0170 8.0170 8.0170 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 515.271 Density (g/cm3): 5.400 MAX. ABS. INTENSITY / VOLUME**2: 79.92377583 RIR: 4.820 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.18 39.80 4.6286 1 1 1 8 31.56 9.06 2.8344 2 2 0 12 37.20 100.00 2.4172 3 1 1 24 38.92 17.06 2.3143 2 2 2 8 45.24 48.88 2.0043 4 0 0 6 49.56 14.01 1.8392 3 3 1 24 56.21 2.94 1.6365 4 2 2 24 59.96 8.67 1.5429 3 3 3 8 59.96 17.88 1.5429 5 1 1 24 65.91 46.64 1.4172 4 4 0 12 69.35 5.92 1.3551 5 3 1 48 74.91 1.16 1.2676 6 2 0 24 78.18 8.95 1.2226 5 3 3 24 79.26 7.53 1.2086 6 2 2 24 83.55 6.87 1.1572 4 4 4 8 86.74 1.96 1.1226 7 1 1 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.