Ni2SiO4 Finger L W, Hazen R M, Yagi T American Mineralogist 64 (1979) 1002-1009 Crystal structures and electron densities of nickel and iron silicate spinels at elevated temperature or pressure P = 31.0 kbar, T = 23 C _database_code_amcsd 0000745 CELL PARAMETERS: 8.0086 8.0086 8.0086 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 513.653 Density (g/cm3): 5.417 MAX. ABS. INTENSITY / VOLUME**2: 80.54492695 RIR: 4.842 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.20 39.78 4.6238 1 1 1 8 31.60 9.08 2.8315 2 2 0 12 37.24 100.00 2.4147 3 1 1 24 38.96 17.16 2.3119 2 2 2 8 45.29 48.62 2.0022 4 0 0 6 49.62 13.88 1.8373 3 3 1 24 56.27 3.00 1.6347 4 2 2 24 60.02 8.69 1.5413 3 3 3 8 60.02 18.10 1.5413 5 1 1 24 65.99 46.80 1.4157 4 4 0 12 69.43 5.90 1.3537 5 3 1 48 75.01 1.21 1.2663 6 2 0 24 78.28 9.09 1.2213 5 3 3 24 79.36 7.70 1.2073 6 2 2 24 83.66 6.83 1.1559 4 4 4 8 86.86 1.94 1.1214 7 1 1 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.