Kanonaite Weiss Z, Bailey S W, Rieder M American Mineralogist 66 (1981) 561-567 Refinement of the crystal structure of kanonaite, (Mn,Al)(Al,Mn)O[SiO4] _database_code_amcsd 0000833 CELL PARAMETERS: 7.9590 8.0470 5.6160 90.000 90.000 90.000 SPACE GROUP: Pnnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 359.683 Density (g/cm3): 3.436 MAX. ABS. INTENSITY / VOLUME**2: 17.31587777 RIR: 1.641 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.66 100.00 5.6587 1 1 0 4 19.27 30.47 4.6053 0 1 1 4 19.34 44.88 4.5887 1 0 1 4 22.30 19.70 3.9861 1 1 1 8 24.80 12.47 3.5908 1 2 0 4 24.96 16.09 3.5671 2 1 0 4 31.62 55.87 2.8294 2 2 0 4 31.87 3.19 2.8080 0 0 2 2 35.31 11.88 2.5419 1 3 0 4 35.53 2.61 2.5268 2 2 1 8 35.63 27.07 2.5196 3 1 0 4 35.70 34.41 2.5153 1 1 2 8 37.15 5.83 2.4204 0 3 1 4 37.49 3.33 2.3988 3 0 1 4 38.89 7.74 2.3157 1 3 1 8 39.12 24.70 2.3027 0 2 2 4 39.19 12.34 2.2988 3 1 1 8 39.27 2.17 2.2943 2 0 2 4 40.74 10.85 2.2149 3 2 0 4 40.79 9.29 2.2120 1 2 2 8 40.90 9.41 2.2064 2 1 2 8 45.51 4.03 1.9931 2 2 2 8 45.59 3.95 1.9898 4 0 0 2 47.05 1.16 1.9316 4 1 0 4 48.25 1.73 1.8862 3 3 0 4 48.30 10.14 1.8845 1 3 2 8 48.55 2.55 1.8753 3 1 2 8 49.47 3.24 1.8425 1 4 1 8 49.93 4.33 1.8266 4 1 1 8 50.02 3.66 1.8233 0 1 3 4 50.06 1.40 1.8223 1 0 3 4 50.86 1.34 1.7954 2 4 0 4 51.08 3.15 1.7881 3 3 1 8 56.25 4.94 1.6354 0 4 2 4 56.70 12.08 1.6235 4 0 2 4 58.51 3.83 1.5775 1 5 0 4 58.99 12.52 1.5658 3 3 2 8 59.17 4.56 1.5615 5 1 0 4 60.02 1.48 1.5414 3 4 1 8 60.21 1.50 1.5371 4 3 1 8 60.29 1.04 1.5351 0 3 3 4 60.53 1.08 1.5296 3 0 3 4 61.01 4.32 1.5187 1 5 1 8 61.28 27.88 1.5126 2 4 2 8 61.52 2.47 1.5073 1 3 3 8 61.60 9.36 1.5055 4 2 2 8 61.65 4.06 1.5045 5 1 1 8 61.73 2.19 1.5027 3 1 3 8 62.22 1.91 1.4920 2 5 0 4 66.04 7.55 1.4147 4 4 0 4 66.61 10.65 1.4040 0 0 4 2 68.19 1.90 1.3753 1 5 2 8 68.79 1.95 1.3647 5 1 2 8 68.91 2.11 1.3627 1 1 4 8 69.61 1.52 1.3506 1 4 3 8 70.93 1.22 1.3287 3 3 3 8 71.62 2.65 1.3176 2 5 2 8 72.14 4.29 1.3094 5 2 2 8 74.69 2.23 1.2709 2 6 0 4 75.21 2.34 1.2634 4 4 2 8 75.46 3.32 1.2598 6 2 0 4 75.61 6.13 1.2577 2 2 4 8 77.20 3.46 1.2356 3 5 2 8 77.59 2.16 1.2305 5 3 2 8 77.70 2.04 1.2290 1 3 4 8 77.89 3.61 1.2264 3 1 4 8 79.14 2.39 1.2102 0 6 2 4 79.45 2.38 1.2063 1 5 3 8 79.99 2.94 1.1994 6 0 2 4 80.02 1.37 1.1991 5 1 3 8 88.24 1.20 1.1074 6 4 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.