Ilmenite Wechsler B A, Prewitt C T American Mineralogist 69 (1984) 176-185 Crystal structure of ilmenite (FeTiO3) at high temperature and high pressure T = 800 C _database_code_amcsd 0000928 CELL PARAMETERS: 5.1280 5.1280 14.1870 90.000 90.000 120.000 SPACE GROUP: R-3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 323.085 Density (g/cm3): 4.678 MAX. ABS. INTENSITY / VOLUME**2: 41.72101750 RIR: 2.904 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 23.64 30.99 3.7641 0 1 2 6 32.30 100.00 2.7714 1 0 4 6 35.00 67.77 2.5640 1 1 0 6 38.06 1.52 2.3645 0 0 6 2 40.00 5.61 2.2540 2 -1 3 6 40.00 16.22 2.2540 1 1 3 6 41.15 1.62 2.1938 0 2 1 6 42.67 1.56 2.1191 2 0 2 6 48.36 33.77 1.8821 0 2 4 6 52.66 24.54 1.7382 2 -1 6 6 52.66 18.25 1.7382 1 1 6 6 55.82 7.43 1.6469 0 1 8 6 56.32 1.80 1.6334 -1 3 2 6 61.08 14.80 1.5172 3 -1 4 6 61.08 10.36 1.5172 2 1 4 6 62.77 24.79 1.4803 3 0 0 6 67.61 2.08 1.3857 2 0 8 6 69.56 8.59 1.3514 1 0 10 6 70.07 1.61 1.3429 1 1 9 6 73.93 5.20 1.2820 2 2 0 6 78.45 1.73 1.2191 -1 3 8 6 78.45 1.28 1.2191 1 2 8 6 78.88 1.01 1.2135 3 1 2 6 80.31 4.23 1.1955 0 2 10 6 82.99 2.26 1.1635 -1 4 4 6 82.99 3.83 1.1635 1 3 4 6 86.32 2.40 1.1270 4 -2 6 6 86.32 3.02 1.1270 2 2 6 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.