Nyboite Raudsepp M, Turnock A C, Hawthorne F C American Mineralogist 72 (1987) 959-964 Characterization of cation ordering in synthetic scandium-fluor-eckermannite, indium-fluor-eckermannite, and scandium-fluor-nyboite by Rietveld structure refinement Sample: FScNY-A3 _database_code_amcsd 0001117 CELL PARAMETERS: 9.8425 18.1570 5.3381 90.000 103.979 90.000 SPACE GROUP: C2/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 925.721 Density (g/cm3): 3.016 MAX. ABS. INTENSITY / VOLUME**2: 5.321427760 RIR: 0.574 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.74 9.96 9.0785 0 2 0 2 10.47 70.78 8.4529 1 1 0 4 17.12 5.09 5.1800 0 0 1 2 17.35 1.14 5.1123 1 3 0 4 18.07 18.93 4.9089 -1 1 1 4 18.58 1.38 4.7755 2 0 0 2 19.56 41.57 4.5392 0 4 0 2 19.73 11.75 4.4992 0 2 1 4 21.96 3.23 4.0479 1 1 1 4 22.06 2.49 4.0295 -2 0 1 2 22.80 13.71 3.8995 -1 3 1 4 24.16 8.91 3.6830 -2 2 1 4 26.02 86.85 3.4240 1 3 1 4 26.26 1.36 3.3943 1 5 0 4 27.10 41.14 3.2901 2 4 0 4 28.46 84.36 3.1358 3 1 0 4 29.52 2.52 3.0262 0 6 0 2 29.58 3.99 3.0197 -3 1 1 4 30.01 29.37 2.9777 2 2 1 4 30.22 7.93 2.9579 -1 5 1 4 31.76 27.32 2.8176 3 3 0 4 32.76 100.00 2.7335 1 5 1 4 32.77 41.87 2.7325 -3 3 1 4 34.32 40.64 2.6130 0 6 1 4 34.63 10.02 2.5900 0 0 2 2 35.11 1.73 2.5562 2 6 0 4 35.20 70.93 2.5494 -2 0 2 2 36.06 1.24 2.4906 0 2 2 4 36.61 1.01 2.4544 -2 2 2 4 36.87 2.00 2.4379 3 1 1 4 37.57 3.43 2.3939 3 5 0 4 38.45 26.06 2.3410 -3 5 1 4 38.81 11.66 2.3203 -4 2 1 4 38.96 25.30 2.3119 -1 7 1 4 39.50 16.97 2.2811 -3 1 2 4 39.54 1.88 2.2791 3 3 1 4 40.59 4.70 2.2228 -2 4 2 4 41.03 8.73 2.1999 1 7 1 4 41.36 34.46 2.1830 2 6 1 4 42.04 9.47 2.1495 -3 3 2 4 43.59 16.18 2.0762 2 0 2 2 44.48 16.19 2.0368 3 5 1 4 44.78 1.65 2.0240 2 2 2 4 44.99 11.87 2.0148 -4 0 2 2 45.08 2.32 2.0109 3 7 0 4 45.85 1.53 1.9793 -3 7 1 4 45.86 3.12 1.9788 1 5 2 4 45.98 4.75 1.9739 1 9 0 4 46.66 4.92 1.9468 4 2 1 4 46.76 2.04 1.9427 -3 5 2 4 47.88 9.15 1.8997 5 1 0 4 48.20 5.36 1.8881 2 4 2 4 48.41 1.83 1.8804 -4 6 1 4 48.53 6.61 1.8759 -1 9 1 4 49.04 1.96 1.8576 -5 3 1 4 49.50 3.68 1.8415 -4 4 2 4 50.07 2.28 1.8216 5 3 0 4 50.25 2.64 1.8157 0 10 0 2 50.28 3.93 1.8146 1 9 1 4 52.42 1.40 1.7456 1 7 2 4 52.45 8.33 1.7447 -5 1 2 4 53.28 1.37 1.7192 -5 5 1 4 53.80 8.31 1.7040 -1 3 3 4 54.03 2.87 1.6972 2 10 0 4 54.06 3.28 1.6963 0 2 3 4 54.10 8.51 1.6952 -2 8 2 4 54.20 1.82 1.6922 -3 1 3 4 54.46 3.36 1.6847 -3 9 1 4 55.18 31.21 1.6645 4 6 1 4 55.89 11.16 1.6450 4 8 0 4 56.58 11.71 1.6265 1 11 0 4 57.19 1.38 1.6107 -6 2 1 4 57.79 27.25 1.5953 -1 5 3 4 57.93 5.10 1.5918 6 0 0 2 58.57 5.07 1.5760 4 0 2 2 58.68 2.25 1.5733 2 10 1 4 58.90 1.60 1.5679 6 2 0 4 59.53 1.49 1.5528 4 2 2 4 60.36 5.14 1.5335 1 9 2 4 60.43 1.01 1.5319 2 8 2 4 60.46 10.41 1.5312 -6 0 2 2 60.72 20.81 1.5252 -2 6 3 4 61.20 6.29 1.5145 5 5 1 4 61.26 13.93 1.5131 0 12 0 2 61.55 2.42 1.5067 -4 8 2 4 61.87 1.78 1.4997 0 6 3 4 62.28 4.40 1.4907 2 2 3 4 62.37 2.55 1.4889 4 4 2 4 62.40 1.11 1.4882 1 5 3 4 62.83 1.93 1.4789 -2 10 2 4 63.48 4.39 1.4654 3 11 0 4 63.48 5.58 1.4654 -1 7 3 4 64.19 3.23 1.4509 -6 4 2 4 64.34 2.48 1.4480 -4 10 1 4 64.47 1.49 1.4453 4 10 0 4 64.76 35.43 1.4396 -6 6 1 4 65.34 2.52 1.4281 -5 3 3 4 66.28 1.48 1.4102 -4 6 3 4 67.83 14.91 1.3817 5 1 2 4 68.93 4.24 1.3623 -5 5 3 4 69.03 3.08 1.3606 7 1 0 4 69.49 7.27 1.3526 1 11 2 4 69.53 5.43 1.3520 2 6 3 4 69.60 3.94 1.3508 5 3 2 4 69.72 1.15 1.3488 -4 10 2 4 70.19 2.68 1.3409 -3 11 2 4 70.61 1.43 1.3339 -2 0 4 2 70.67 2.28 1.3330 -1 9 3 4 70.79 1.51 1.3310 7 3 0 4 71.27 2.59 1.3232 -5 9 2 4 71.28 7.29 1.3231 -1 1 4 4 72.04 7.05 1.3109 -7 5 1 4 72.32 6.87 1.3065 0 12 2 4 72.67 18.20 1.3012 -2 12 2 4 73.01 2.56 1.2959 -1 3 4 4 73.07 4.24 1.2950 0 0 4 2 73.31 3.10 1.2913 6 6 1 4 74.20 1.08 1.2781 4 12 0 4 74.43 5.68 1.2747 -4 0 4 2 77.08 1.04 1.2374 -1 13 2 4 77.28 2.67 1.2346 -2 14 1 4 77.83 1.66 1.2272 -4 4 4 4 79.81 9.48 1.2017 -5 11 2 4 80.44 1.36 1.1939 8 0 0 2 81.59 4.37 1.1799 2 0 4 2 82.39 1.14 1.1705 -6 10 2 4 82.89 2.00 1.1647 4 6 3 4 83.12 1.21 1.1621 1 15 1 4 83.17 1.48 1.1615 2 10 3 4 83.29 1.01 1.1602 -8 4 2 4 86.02 3.14 1.1302 7 9 0 4 86.04 1.55 1.1299 5 3 3 4 86.28 2.05 1.1275 5 13 0 4 87.53 1.54 1.1145 -6 4 4 4 88.13 1.04 1.1085 0 16 1 4 88.22 2.67 1.1076 3 1 4 4 88.29 1.36 1.1069 -7 7 3 4 88.48 1.29 1.1050 3 13 2 4 89.35 1.81 1.0965 5 5 3 4 89.78 1.11 1.0923 -5 13 2 4 89.87 3.04 1.0915 4 12 2 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.