Boggsite Pluth J J, Smith J V American Mineralogist 75 (1990) 501-507 Crystal structure of boggsite, a new high-silica zeolite with the first three-dimensional channel system bounded by both 12- and 10-rings _database_code_amcsd 0001303 20.236 23.798 12.798 90 90 90 Imma atom x y z occ U(1,1) U(2,2) U(3,3) U(1,2) U(1,3) U(2,3) Si1 .18881 .18550 .6719 .81 .0189 .0140 .0196 -.0007 .0007 -.0024 Al1 .18881 .18550 .6719 .19 .0189 .0140 .0196 -.0007 .0007 -.0024 Si2 .19006 .02407 .3297 .81 .0214 .0226 .0145 .0001 -.0028 -.0002 Al2 .19006 .02407 .3297 .19 .0214 .0226 .0145 .0001 -.0028 -.0002 Si3 .07689 .18517 .8357 .81 .0164 .0123 .0204 .0003 .0006 .0021 Al3 .07689 .18517 .8357 .19 .0164 .0123 .0204 .0003 .0006 .0021 Si4 .07768 .02210 .1643 .81 .0154 .0226 .0155 .0001 .0007 .0012 Al4 .07768 .02210 .1643 .19 .0154 .0226 .0155 .0001 .0007 .0012 Si5 .22108 .08300 .5378 .81 .0169 .0171 .0176 -.0012 .0007 -.0060 Al5 .22108 .08300 .5378 .19 .0169 .0171 .0176 -.0012 .0007 -.0060 Si6 .12270 .08371 .9656 .81 .0175 .0166 .0176 -.0017 -.0002 .0037 Al6 .12270 .08371 .9656 .19 .0175 .0166 .0176 -.0017 -.0002 .0037 O1 .1882 .25 .6291 .046 .013 .032 0 .002 0 O2 .1194 .1707 .7322 .028 .034 .041 -.004 .009 -.009 O3 .1950 .1456 .5679 .053 .025 .026 .006 0 -.008 O4 .1900 .0702 .4236 .051 .037 .020 .007 -.008 -.011 O5 .1194 .0319 .2722 .024 .059 .026 -.001 -.008 -.004 O6 .0893 .25 .8731 .037 .017 .031 0 -.014 0 O7 0 .1738 .8043 .012 .033 .049 0 0 -.013 O8 0 .0263 .1968 .018 .070 .033 0 0 -.004 O9 .1944 .0379 .6204 .104 .028 .030 -.013 .016 .008 O10 .0978 .1464 .9327 .069 .015 .034 .006 -.006 .008 O11 .0959 .0725 .0813 .067 .037 .027 -.007 .016 .008 O12 .2007 .0800 .9682 .014 .103 .096 -.002 .004 .044 O13 .0949 .0395 .8847 .079 .025 .035 -.011 -.014 -.004 O14 .25 .1755 .75 .039 .033 .050 0 -.022 0 O15 .25 -.0375 .75 .027 .069 .031 0 -.010 0 Wat1 0 .1735 .136 1.85 Wat2 .1936 .1701 .203 1.35 Wat3 .1930 .25 .057 .920 Wat4 .1074 .1754 .372 1.16 Wat5 0 .1750 .570 3.20 Wat6 0 .0284 .429 .910 Wat7 .0562 .1147 .410 .630 Wat8 .0431 .0812 .626 .770 Wat9 .1490 .25 .237 .500 Wat10 .1060 .25 .086 .610 Wat11 .2060 .25 .401 1.32