Clinoptilolite-Ca Smyth J R, Spaid A T, Bish D L American Mineralogist 75 (1990) 522-528 Crystal structures of a natural and a Cs-exchanged clinoptilolite natural sample _database_code_amcsd 0001304 17.633 17.941 7.400 90 116.39 90 C2/m atom x y z occ B(1,1) B(2,2) B(3,3) B(1,2) B(1,3) B(2,3) Si1 .1789 .1705 .0953 .87 .00062 .00104 .0070 -.00004 .00063 .00018 Al1 .1789 .1705 .0953 .13 .00062 .00104 .0070 -.00004 .00063 .00018 Si2 .2131 .4104 .5030 .67 .00092 .00072 .0081 .00006 .00087 .00003 Al2 .2131 .4104 .5030 .33 .00092 .00072 .0081 .00006 .00087 .00003 Si3 .2080 .1907 .7152 .90 .00087 .00093 .0067 .00002 .00081 .00007 Al3 .2080 .1907 .7152 .10 .00087 .00093 .0067 .00002 .00081 .00007 Si4 .0654 .2989 .4129 .92 .00065 .00103 .0071 .00000 .00066 .0001 Al4 .0654 .2989 .4129 .08 .00065 .00103 .0071 .00000 .00066 .0001 Si5 0 .2160 0 .91 .00045 .00116 .0072 0 .0003 0 Al5 0 .2160 0 .09 .00045 .00116 .0072 0 .0003 0 Na1 .1478 0 .6661 .5 .0075 .0027 .0320 0 .0052 0 Ca1 .1478 0 .6661 .5 .0075 .0027 .0320 0 .0052 0 Na2 .0404 .5 .2167 .39 .0015 .0022 .0293 0 -.0004 0 Ca2 .0404 .5 .2167 .39 .0015 .0022 .0293 0 -.0004 0 K3 .2344 .5 .0252 .64 .0116 .0037 .0780 0 .0218 0 O1 .1973 .5 .4571 .0029 .0008 .0180 0 .0018 0 O2 .2320 .1212 .6138 .0022 .0020 .0159 -.0003 .0033 -.0019 O3 .1835 .1565 .8859 .0029 .0021 .0138 -.0003 .0029 -.0001 O4 .2356 .1065 .2518 .0022 .0018 .0146 .0007 .0024 .0004 O5 0 .3245 .5 .0026 .0024 .0212 0 .0048 0 O6 .0811 .1614 .0570 .0009 .0015 .0187 -.0001 .0017 -.0001 O7 .1274 .2343 .5484 .0025 .0025 .0163 .0007 .0001 .0015 O8 .0110 .2682 .1857 .0017 .0026 .0148 .0002 .0015 -.0017 O9 .2119 .2534 .1830 .0015 .0015 .0199 -.0005 .0023 -.0014 O10 .1174 .3723 .4079 .0016 .0016 .0200 -.0005 .0026 -.0002 Wat2 .0798 0 .8531 .98 .0158 .0105 .2570 0 -.0037 0 Wat3 .0798 .4190 .9655 .89 .0060 .0045 .0385 -.0007 -.0006 .0032 Wat4 0 .5 .5 .0058 .0035 .0562 0 .0082 0 Wat5 .0202 .0901 .525 .36 .0042 .0067 .1480 -.0022 -.0008 .0126 Wat6 .0865 0 .2654 .81 .0085 .0090 .1010 0 .0159 0