Spinel Peterson R C, Lager G A, Hitterman R L American Mineralogist 76 (1991) 1455-1458 A time-of-flight neutron powder diffraction study of MgAl2O4 at temperatures up to 1273 K sample W, T = 873 K _database_code_amcsd 0001400 CELL PARAMETERS: 8.1250 8.1250 8.1250 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 536.379 Density (g/cm3): 3.524 MAX. ABS. INTENSITY / VOLUME**2: 17.77216638 RIR: 1.642 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.92 31.99 4.6910 1 1 1 8 31.13 33.98 2.8726 2 2 0 12 36.68 100.00 2.4498 3 1 1 24 38.38 1.41 2.3455 2 2 2 8 44.61 55.50 2.0313 4 0 0 6 55.40 9.18 1.6585 4 2 2 24 59.08 2.92 1.5637 3 3 3 8 59.08 40.86 1.5637 5 1 1 24 64.92 67.25 1.4363 4 4 0 12 68.30 2.56 1.3734 5 3 1 48 73.75 2.77 1.2847 6 2 0 24 76.95 8.91 1.2391 5 3 3 24 82.20 5.70 1.1727 4 4 4 8 85.31 2.21 1.1377 5 5 1 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.