LiScSiO4 Hazen R M, Downs R T, Finger L W American Mineralogist 81 (1996) 327-334 High-pressure crystal chemistry of LiScSiO4: An olivine with nearly isotropic compression Sample: #0, P = 0.0 GPa _database_code_amcsd 0001777 CELL PARAMETERS: 4.8168 10.4317 5.9650 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 299.726 Density (g/cm3): 3.190 MAX. ABS. INTENSITY / VOLUME**2: 10.94467255 RIR: 1.117 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.00 28.70 5.2158 0 2 0 2 20.31 64.14 4.3731 1 1 0 4 22.65 33.83 3.9265 0 2 1 4 23.74 13.06 3.7475 1 0 1 4 25.17 7.36 3.5387 1 2 0 4 25.25 69.03 3.5268 1 1 1 8 29.35 5.18 3.0434 1 2 1 8 29.96 59.07 2.9825 0 0 2 2 31.74 19.05 2.8194 1 3 0 4 35.21 100.00 2.5490 1 3 1 8 36.46 30.65 2.4640 1 1 2 8 37.64 12.75 2.3895 0 4 1 4 38.36 7.00 2.3467 2 1 0 4 39.29 19.40 2.2934 1 4 0 4 39.52 26.45 2.2805 1 2 2 8 41.29 7.21 2.1866 2 2 0 4 41.34 16.27 2.1838 2 1 1 8 44.11 1.35 2.0530 2 2 1 8 44.21 1.33 2.0488 1 3 2 8 46.24 1.56 1.9632 0 4 2 4 48.59 15.87 1.8738 2 0 2 4 50.04 8.85 1.8229 1 5 1 8 50.42 11.32 1.8100 1 1 3 8 51.66 10.46 1.7693 2 4 0 4 51.85 34.34 1.7634 2 2 2 8 52.64 2.79 1.7386 0 6 0 2 52.81 4.37 1.7334 1 2 3 8 54.06 16.52 1.6963 2 4 1 8 55.01 14.25 1.6692 0 6 1 4 55.73 1.13 1.6495 2 3 2 8 56.65 22.57 1.6249 1 3 3 8 58.36 9.47 1.5812 0 4 3 4 59.63 1.31 1.5504 3 0 1 4 60.31 1.60 1.5345 3 2 0 4 60.36 6.42 1.5336 3 1 1 8 60.75 3.23 1.5246 2 5 1 8 60.88 1.31 1.5217 2 4 2 8 61.09 2.86 1.5170 2 1 3 8 61.76 22.34 1.5020 0 6 2 4 62.26 15.77 1.4913 0 0 4 2 62.49 1.58 1.4861 3 2 1 8 65.57 6.85 1.4237 1 7 0 4 65.97 12.65 1.4160 3 3 1 8 66.21 3.08 1.4114 1 1 4 8 66.31 4.48 1.4097 2 6 0 4 67.97 2.07 1.3791 1 5 3 8 68.38 1.72 1.3719 2 6 1 8 68.64 4.02 1.3673 3 4 0 4 68.80 11.32 1.3645 3 2 2 8 70.69 3.26 1.3327 3 4 1 8 71.36 2.14 1.3218 2 4 3 8 71.58 2.13 1.3182 1 3 4 8 72.12 3.30 1.3096 3 3 2 8 72.17 5.44 1.3088 0 6 3 4 73.74 7.69 1.2848 1 7 2 8 74.90 1.31 1.2679 2 0 4 4 75.23 1.17 1.2630 1 6 3 8 76.14 1.00 1.2502 1 4 4 8 76.22 2.03 1.2492 3 0 3 4 76.86 1.29 1.2403 3 1 3 8 77.21 2.12 1.2355 2 5 3 8 77.47 2.33 1.2320 2 2 4 8 79.61 2.58 1.2042 4 0 0 2 81.95 5.93 1.1756 3 3 3 8 82.15 1.53 1.1733 4 2 0 4 82.40 1.63 1.1704 3 5 2 8 82.75 2.11 1.1663 2 7 2 8 83.04 1.28 1.1630 0 2 5 4 83.33 1.15 1.1596 1 8 2 8 83.55 2.21 1.1571 3 6 1 8 84.11 1.08 1.1509 1 1 5 8 85.08 2.47 1.1403 2 4 4 8 85.86 2.19 1.1319 0 6 4 4 86.33 1.28 1.1269 1 9 0 4 86.36 2.71 1.1266 3 4 3 8 86.41 1.53 1.1261 2 8 1 8 87.95 2.27 1.1103 4 1 2 8 88.25 1.72 1.1073 1 9 1 8 89.12 5.58 1.0987 1 3 5 8 89.79 1.57 1.0923 3 7 0 4 89.83 1.68 1.0919 4 2 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.