LiScSiO4 Hazen R M, Downs R T, Finger L W American Mineralogist 81 (1996) 327-334 High-pressure crystal chemistry of LiScSiO4: An olivine with nearly isotropic compression Sample: #2, P = 0.23 GPa _database_code_amcsd 0001780 CELL PARAMETERS: 4.8190 10.4333 5.9672 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 300.019 Density (g/cm3): 3.187 MAX. ABS. INTENSITY / VOLUME**2: 11.08229723 RIR: 1.132 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.00 27.56 5.2167 0 2 0 2 20.30 62.29 4.3749 1 1 0 4 22.64 32.33 3.9274 0 2 1 4 23.73 12.46 3.7491 1 0 1 4 25.16 7.18 3.5398 1 2 0 4 25.24 67.39 3.5282 1 1 1 8 29.34 5.25 3.0444 1 2 1 8 29.95 57.89 2.9836 0 0 2 2 31.73 19.54 2.8201 1 3 0 4 35.20 100.00 2.5497 1 3 1 8 36.45 29.66 2.4649 1 1 2 8 37.64 13.08 2.3900 0 4 1 4 38.34 7.24 2.3477 2 1 0 4 39.28 20.05 2.2939 1 4 0 4 39.50 26.93 2.2813 1 2 2 8 41.27 7.40 2.1874 2 2 0 4 41.33 15.05 2.1847 2 1 1 8 44.09 1.18 2.0538 2 2 1 8 44.19 1.38 2.0495 1 3 2 8 46.23 1.66 1.9637 0 4 2 4 48.57 15.65 1.8746 2 0 2 4 50.03 8.43 1.8233 1 5 1 8 50.40 11.23 1.8107 1 1 3 8 51.64 10.22 1.7699 2 4 0 4 51.83 34.94 1.7641 2 2 2 8 52.63 2.70 1.7389 0 6 0 2 52.79 4.35 1.7341 1 2 3 8 54.04 16.84 1.6968 2 4 1 8 55.00 14.06 1.6694 0 6 1 4 55.70 1.08 1.6501 2 3 2 8 56.63 22.53 1.6254 1 3 3 8 58.34 9.47 1.5816 0 4 3 4 59.60 1.09 1.5511 3 0 1 4 60.29 1.62 1.5352 3 2 0 4 60.33 6.40 1.5343 3 1 1 8 60.73 3.13 1.5250 2 5 1 8 60.85 1.17 1.5222 2 4 2 8 61.06 2.60 1.5176 2 1 3 8 61.75 22.41 1.5024 0 6 2 4 62.23 15.88 1.4918 0 0 4 2 62.47 1.50 1.4868 3 2 1 8 65.56 6.81 1.4239 1 7 0 4 65.94 12.55 1.4166 3 3 1 8 66.18 2.99 1.4120 1 1 4 8 66.29 4.38 1.4100 2 6 0 4 66.74 1.08 1.4016 3 1 2 8 67.95 1.97 1.3795 1 5 3 8 68.36 1.72 1.3722 2 6 1 8 68.62 4.15 1.3678 3 4 0 4 68.77 11.50 1.3651 3 2 2 8 70.66 3.25 1.3332 3 4 1 8 71.33 2.24 1.3222 2 4 3 8 71.55 2.21 1.3187 1 3 4 8 72.09 3.36 1.3102 3 3 2 8 72.15 5.38 1.3091 0 6 3 4 73.73 7.68 1.2851 1 7 2 8 74.86 1.23 1.2684 2 0 4 4 75.21 1.13 1.2634 1 6 3 8 76.11 1.16 1.2506 1 4 4 8 76.18 1.82 1.2497 3 0 3 4 76.82 1.27 1.2408 3 1 3 8 77.18 2.06 1.2359 2 5 3 8 77.44 2.36 1.2325 2 2 4 8 79.57 2.76 1.2047 4 0 0 2 81.92 5.93 1.1761 3 3 3 8 82.10 1.41 1.1739 4 2 0 4 82.37 1.67 1.1708 3 5 2 8 82.72 2.05 1.1666 2 7 2 8 83.00 1.24 1.1634 0 2 5 4 83.31 1.19 1.1599 1 8 2 8 83.52 2.09 1.1575 3 6 1 8 84.07 1.09 1.1514 1 1 5 8 85.04 2.48 1.1407 2 4 4 8 85.83 2.09 1.1322 0 6 4 4 86.31 1.28 1.1271 1 9 0 4 86.32 2.71 1.1270 3 4 3 8 86.39 1.61 1.1263 2 8 1 8 87.90 2.40 1.1108 4 1 2 8 88.23 1.62 1.1075 1 9 1 8 89.08 5.56 1.0991 1 3 5 8 89.75 1.66 1.0926 3 7 0 4 89.78 1.53 1.0924 4 2 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.