LiScSiO4 Hazen R M, Downs R T, Finger L W American Mineralogist 81 (1996) 327-334 High-pressure crystal chemistry of LiScSiO4: An olivine with nearly isotropic compression Sample: #2, P = 0.99 GPa _database_code_amcsd 0001781 CELL PARAMETERS: 4.8040 10.4117 5.9533 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 297.771 Density (g/cm3): 3.211 MAX. ABS. INTENSITY / VOLUME**2: 11.06390115 RIR: 1.122 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.03 27.09 5.2059 0 2 0 2 20.36 63.00 4.3621 1 1 0 4 22.69 32.47 3.9189 0 2 1 4 23.80 12.24 3.7386 1 0 1 4 25.23 7.33 3.5305 1 2 0 4 25.31 69.28 3.5186 1 1 1 8 29.41 5.32 3.0367 1 2 1 8 30.02 58.68 2.9766 0 0 2 2 31.81 18.50 2.8132 1 3 0 4 35.29 100.00 2.5435 1 3 1 8 36.55 30.04 2.4587 1 1 2 8 37.72 13.46 2.3849 0 4 1 4 38.46 7.36 2.3405 2 1 0 4 39.37 20.03 2.2886 1 4 0 4 39.60 26.37 2.2757 1 2 2 8 41.40 7.35 2.1810 2 2 0 4 41.45 15.78 2.1782 2 1 1 8 44.23 1.17 2.0479 2 2 1 8 44.30 1.24 2.0446 1 3 2 8 46.34 1.76 1.9594 0 4 2 4 48.71 15.68 1.8693 2 0 2 4 50.15 8.41 1.8192 1 5 1 8 50.53 11.30 1.8063 1 1 3 8 51.79 10.32 1.7652 2 4 0 4 51.98 34.28 1.7593 2 2 2 8 52.75 3.01 1.7353 0 6 0 2 52.93 4.33 1.7299 1 2 3 8 54.20 16.25 1.6924 2 4 1 8 55.13 13.26 1.6660 0 6 1 4 55.86 1.03 1.6458 2 3 2 8 56.77 22.48 1.6216 1 3 3 8 58.48 9.51 1.5781 0 4 3 4 59.81 1.10 1.5464 3 0 1 4 60.49 1.63 1.5306 3 2 0 4 60.53 6.27 1.5296 3 1 1 8 60.90 3.33 1.5212 2 5 1 8 61.03 1.30 1.5183 2 4 2 8 61.24 2.78 1.5136 2 1 3 8 61.89 22.72 1.4991 0 6 2 4 62.39 15.71 1.4883 0 0 4 2 62.67 1.78 1.4824 3 2 1 8 65.72 6.90 1.4208 1 7 0 4 66.16 12.59 1.4125 3 3 1 8 66.36 3.04 1.4086 1 1 4 8 66.47 4.34 1.4066 2 6 0 4 68.13 1.96 1.3764 1 5 3 8 68.55 1.69 1.3689 2 6 1 8 68.84 4.04 1.3639 3 4 0 4 68.99 11.27 1.3612 3 2 2 8 70.88 3.22 1.3295 3 4 1 8 71.54 2.17 1.3189 2 4 3 8 71.75 2.04 1.3156 1 3 4 8 72.32 3.18 1.3065 3 3 2 8 72.34 5.05 1.3063 0 6 3 4 73.91 7.82 1.2823 1 7 2 8 75.09 1.26 1.2651 2 0 4 4 75.41 1.08 1.2605 1 6 3 8 76.32 1.09 1.2477 1 4 4 8 76.43 1.79 1.2462 3 0 3 4 77.08 1.28 1.2374 3 1 3 8 77.41 2.14 1.2329 2 5 3 8 77.67 2.35 1.2294 2 2 4 8 79.87 2.56 1.2010 4 0 0 2 82.19 5.92 1.1729 3 3 3 8 82.41 1.44 1.1703 4 2 0 4 82.63 1.58 1.1677 3 5 2 8 82.96 2.01 1.1639 2 7 2 8 83.24 1.21 1.1607 0 2 5 4 83.54 1.11 1.1573 1 8 2 8 83.79 2.10 1.1545 3 6 1 8 84.31 1.10 1.1486 1 1 5 8 85.30 2.46 1.1379 2 4 4 8 86.06 2.26 1.1297 0 6 4 4 86.54 1.21 1.1247 1 9 0 4 86.61 2.66 1.1240 3 4 3 8 86.64 1.55 1.1237 2 8 1 8 88.23 2.40 1.1074 4 1 2 8 88.46 1.76 1.1052 1 9 1 8 89.35 5.55 1.0965 1 3 5 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.