LiScSiO4 Hazen R M, Downs R T, Finger L W American Mineralogist 81 (1996) 327-334 High-pressure crystal chemistry of LiScSiO4: An olivine with nearly isotropic compression Sample: #1, P = 1.46 GPa _database_code_amcsd 0001782 CELL PARAMETERS: 4.7996 10.3925 5.9443 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 296.501 Density (g/cm3): 3.225 MAX. ABS. INTENSITY / VOLUME**2: 11.22761288 RIR: 1.134 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.06 26.52 5.1962 0 2 0 2 20.38 62.46 4.3574 1 1 0 4 22.73 32.43 3.9122 0 2 1 4 23.83 13.07 3.7343 1 0 1 4 25.26 7.61 3.5257 1 2 0 4 25.34 68.80 3.5143 1 1 1 8 29.46 5.34 3.0324 1 2 1 8 30.07 58.47 2.9722 0 0 2 2 31.86 18.55 2.8089 1 3 0 4 35.34 100.00 2.5397 1 3 1 8 36.60 29.53 2.4553 1 1 2 8 37.79 13.09 2.3807 0 4 1 4 38.50 7.25 2.3383 2 1 0 4 39.44 19.63 2.2848 1 4 0 4 39.66 26.82 2.2724 1 2 2 8 41.45 7.65 2.1787 2 2 0 4 41.50 15.88 2.1760 2 1 1 8 44.28 1.26 2.0456 2 2 1 8 44.37 1.29 2.0415 1 3 2 8 46.42 1.90 1.9561 0 4 2 4 48.77 15.67 1.8671 2 0 2 4 50.24 8.50 1.8161 1 5 1 8 50.61 11.43 1.8037 1 1 3 8 51.86 10.83 1.7629 2 4 0 4 52.05 34.45 1.7571 2 2 2 8 52.86 2.99 1.7321 0 6 0 2 53.01 4.40 1.7273 1 2 3 8 54.28 16.52 1.6901 2 4 1 8 55.24 13.56 1.6629 0 6 1 4 55.94 1.08 1.6436 2 3 2 8 56.87 22.61 1.6191 1 3 3 8 58.59 9.51 1.5755 0 4 3 4 59.87 1.12 1.5449 3 0 1 4 60.55 1.62 1.5290 3 2 0 4 60.60 6.59 1.5281 3 1 1 8 61.00 3.38 1.5190 2 5 1 8 61.12 1.32 1.5162 2 4 2 8 61.32 2.80 1.5117 2 1 3 8 62.01 23.09 1.4965 0 6 2 4 62.50 15.85 1.4861 0 0 4 2 62.74 1.67 1.4808 3 2 1 8 65.85 6.85 1.4183 1 7 0 4 66.24 12.43 1.4109 3 3 1 8 66.47 3.13 1.4065 1 1 4 8 66.58 4.48 1.4045 2 6 0 4 68.25 1.98 1.3741 1 5 3 8 68.67 1.64 1.3668 2 6 1 8 68.93 4.24 1.3623 3 4 0 4 69.08 11.73 1.3597 3 2 2 8 70.98 3.19 1.3279 3 4 1 8 71.65 2.19 1.3171 2 4 3 8 71.87 2.05 1.3136 1 3 4 8 72.42 3.33 1.3050 3 3 2 8 72.48 5.08 1.3041 0 6 3 4 74.06 8.12 1.2801 1 7 2 8 75.20 1.21 1.2634 2 0 4 4 75.55 1.27 1.2584 1 6 3 8 76.46 1.10 1.2458 1 4 4 8 76.53 1.90 1.2448 3 0 3 4 77.18 1.34 1.2359 3 1 3 8 77.54 2.18 1.2311 2 5 3 8 77.80 2.52 1.2277 2 2 4 8 79.95 2.61 1.1999 4 0 0 2 82.31 5.97 1.1714 3 3 3 8 82.51 1.55 1.1691 4 2 0 4 82.77 1.70 1.1661 3 5 2 8 83.12 2.06 1.1621 2 7 2 8 83.40 1.28 1.1589 0 2 5 4 83.71 1.25 1.1553 1 8 2 8 83.93 2.18 1.1529 3 6 1 8 84.47 1.13 1.1469 1 1 5 8 85.45 2.57 1.1362 2 4 4 8 86.24 2.35 1.1279 0 6 4 4 86.73 1.26 1.1227 1 9 0 4 86.75 2.78 1.1226 3 4 3 8 86.81 1.58 1.1219 2 8 1 8 88.35 2.47 1.1063 4 1 2 8 88.66 1.79 1.1032 1 9 1 8 89.52 5.74 1.0948 1 3 5 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.