LiScSiO4 Hazen R M, Downs R T, Finger L W American Mineralogist 81 (1996) 327-334 High-pressure crystal chemistry of LiScSiO4: An olivine with nearly isotropic compression Sample: #2, P = 2.17 GPa _database_code_amcsd 0001783 CELL PARAMETERS: 4.7918 10.3784 5.9365 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 295.229 Density (g/cm3): 3.239 MAX. ABS. INTENSITY / VOLUME**2: 11.38805801 RIR: 1.145 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.09 26.35 5.1892 0 2 0 2 20.41 59.68 4.3505 1 1 0 4 22.76 31.72 3.9070 0 2 1 4 23.86 12.06 3.7287 1 0 1 4 25.30 7.33 3.5204 1 2 0 4 25.38 67.67 3.5091 1 1 1 8 29.50 5.55 3.0280 1 2 1 8 30.11 57.25 2.9683 0 0 2 2 31.91 18.09 2.8049 1 3 0 4 35.39 100.00 2.5361 1 3 1 8 36.65 29.07 2.4519 1 1 2 8 37.84 12.98 2.3774 0 4 1 4 38.57 7.03 2.3345 2 1 0 4 39.50 19.60 2.2816 1 4 0 4 39.72 26.96 2.2693 1 2 2 8 41.51 7.50 2.1752 2 2 0 4 41.57 14.58 2.1726 2 1 1 8 44.35 1.09 2.0424 2 2 1 8 44.44 1.30 2.0387 1 3 2 8 46.49 1.80 1.9535 0 4 2 4 48.85 15.15 1.8643 2 0 2 4 50.31 8.23 1.8136 1 5 1 8 50.68 10.89 1.8013 1 1 3 8 51.95 10.79 1.7602 2 4 0 4 52.13 34.37 1.7545 2 2 2 8 52.93 3.00 1.7297 0 6 0 2 53.09 4.21 1.7250 1 2 3 8 54.36 16.00 1.6876 2 4 1 8 55.32 13.14 1.6607 0 6 1 4 56.03 1.01 1.6412 2 3 2 8 56.95 22.36 1.6169 1 3 3 8 58.68 9.07 1.5734 0 4 3 4 60.66 1.64 1.5266 3 2 0 4 60.70 6.31 1.5257 3 1 1 8 61.10 3.33 1.5167 2 5 1 8 61.22 1.24 1.5140 2 4 2 8 61.42 2.62 1.5095 2 1 3 8 62.11 22.94 1.4945 0 6 2 4 62.59 15.74 1.4841 0 0 4 2 62.86 1.65 1.4785 3 2 1 8 65.95 6.69 1.4164 1 7 0 4 66.36 11.94 1.4087 3 3 1 8 66.57 2.89 1.4046 1 1 4 8 66.69 4.25 1.4024 2 6 0 4 68.36 1.97 1.3723 1 5 3 8 68.78 1.52 1.3649 2 6 1 8 69.05 4.20 1.3602 3 4 0 4 69.20 11.79 1.3576 3 2 2 8 71.11 3.26 1.3258 3 4 1 8 71.77 2.17 1.3152 2 4 3 8 71.98 2.06 1.3118 1 3 4 8 72.55 2.92 1.3030 3 3 2 8 72.59 4.89 1.3023 0 6 3 4 74.18 7.56 1.2783 1 7 2 8 75.33 1.13 1.2617 2 0 4 4 75.68 1.11 1.2567 1 6 3 8 76.58 1.16 1.2441 1 4 4 8 76.67 1.73 1.2429 3 0 3 4 77.32 1.37 1.2341 3 1 3 8 77.67 2.07 1.2293 2 5 3 8 77.93 2.34 1.2260 2 2 4 8 80.11 2.71 1.1980 4 0 0 2 82.46 5.71 1.1697 3 3 3 8 82.67 1.38 1.1673 4 2 0 4 82.92 1.62 1.1644 3 5 2 8 83.26 1.90 1.1604 2 7 2 8 83.53 1.22 1.1574 0 2 5 4 83.85 1.16 1.1538 1 8 2 8 84.08 2.02 1.1512 3 6 1 8 84.61 1.11 1.1454 1 1 5 8 85.60 2.64 1.1346 2 4 4 8 86.38 2.22 1.1264 0 6 4 4 86.88 1.21 1.1211 1 9 0 4 86.91 2.77 1.1209 3 4 3 8 86.97 1.53 1.1203 2 8 1 8 88.52 2.39 1.1046 4 1 2 8 88.82 1.76 1.1017 1 9 1 8 89.67 5.58 1.0934 1 3 5 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.