LiScSiO4 Hazen R M, Downs R T, Finger L W American Mineralogist 81 (1996) 327-334 High-pressure crystal chemistry of LiScSiO4: An olivine with nearly isotropic compression Sample: #2, P = 3.02 GPa _database_code_amcsd 0001784 CELL PARAMETERS: 4.7802 10.3514 5.9224 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 293.051 Density (g/cm3): 3.263 MAX. ABS. INTENSITY / VOLUME**2: 11.62023686 RIR: 1.160 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.13 25.09 5.1757 0 2 0 2 20.46 58.70 4.3398 1 1 0 4 22.82 31.17 3.8972 0 2 1 4 23.92 12.07 3.7197 1 0 1 4 25.36 7.66 3.5116 1 2 0 4 25.44 67.52 3.5006 1 1 1 8 29.57 5.57 3.0206 1 2 1 8 30.18 56.85 2.9612 0 0 2 2 31.99 16.63 2.7977 1 3 0 4 35.49 100.00 2.5297 1 3 1 8 36.74 30.03 2.4460 1 1 2 8 37.94 13.31 2.3713 0 4 1 4 38.66 6.31 2.3288 2 1 0 4 39.60 19.78 2.2758 1 4 0 4 39.82 26.66 2.2638 1 2 2 8 41.62 7.29 2.1699 2 2 0 4 41.67 14.10 2.1673 2 1 1 8 44.47 1.24 2.0375 2 2 1 8 44.55 1.39 2.0336 1 3 2 8 46.61 1.90 1.9486 0 4 2 4 48.98 15.13 1.8599 2 0 2 4 50.45 7.81 1.8090 1 5 1 8 50.81 10.58 1.7970 1 1 3 8 52.09 11.09 1.7558 2 4 0 4 52.27 34.55 1.7503 2 2 2 8 53.08 3.07 1.7252 0 6 0 2 53.23 4.34 1.7208 1 2 3 8 54.51 15.81 1.6834 2 4 1 8 55.48 12.52 1.6564 0 6 1 4 57.10 22.47 1.6130 1 3 3 8 58.83 9.38 1.5696 0 4 3 4 60.83 1.54 1.5229 3 2 0 4 60.87 6.44 1.5220 3 1 1 8 61.27 3.35 1.5129 2 5 1 8 61.39 1.26 1.5103 2 4 2 8 61.59 2.67 1.5059 2 1 3 8 62.28 23.32 1.4907 0 6 2 4 62.76 15.71 1.4806 0 0 4 2 63.03 1.92 1.4749 3 2 1 8 66.14 6.94 1.4127 1 7 0 4 66.54 11.37 1.4053 3 3 1 8 66.75 2.91 1.4013 1 1 4 8 66.88 4.28 1.3989 2 6 0 4 68.55 1.92 1.3689 1 5 3 8 68.98 1.48 1.3614 2 6 1 8 69.25 4.48 1.3568 3 4 0 4 69.40 12.33 1.3543 3 2 2 8 71.31 3.27 1.3226 3 4 1 8 71.97 2.02 1.3120 2 4 3 8 72.19 1.96 1.3086 1 3 4 8 72.76 2.59 1.2998 3 3 2 8 72.80 4.69 1.2991 0 6 3 4 74.40 7.74 1.2750 1 7 2 8 75.54 1.10 1.2587 2 0 4 4 75.90 1.17 1.2536 1 6 3 8 76.80 1.16 1.2411 1 4 4 8 76.89 1.83 1.2399 3 0 3 4 77.54 1.54 1.2311 3 1 3 8 77.90 2.05 1.2263 2 5 3 8 78.15 2.34 1.2230 2 2 4 8 80.35 2.81 1.1951 4 0 0 2 82.70 5.49 1.1669 3 3 3 8 82.92 1.47 1.1644 4 2 0 4 83.17 1.71 1.1615 3 5 2 8 83.52 1.76 1.1575 2 7 2 8 83.78 1.27 1.1546 0 2 5 4 84.12 1.19 1.1508 1 8 2 8 84.34 2.14 1.1483 3 6 1 8 84.85 1.15 1.1427 1 1 5 8 85.86 2.75 1.1319 2 4 4 8 86.65 2.32 1.1236 0 6 4 4 87.17 1.19 1.1182 1 9 0 4 87.17 2.90 1.1182 3 4 3 8 87.24 1.58 1.1174 2 8 1 8 88.79 2.43 1.1019 4 1 2 8 89.11 1.85 1.0988 1 9 1 8 89.95 5.70 1.0908 1 3 5 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.