LiScSiO4 Hazen R M, Downs R T, Finger L W American Mineralogist 81 (1996) 327-334 High-pressure crystal chemistry of LiScSiO4: An olivine with nearly isotropic compression Sample: #2, P = 4.51 GPa _database_code_amcsd 0001786 CELL PARAMETERS: 4.7611 10.3072 5.9006 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 289.564 Density (g/cm3): 3.302 MAX. ABS. INTENSITY / VOLUME**2: 11.75965997 RIR: 1.160 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.21 24.25 5.1536 0 2 0 2 20.55 55.16 4.3223 1 1 0 4 22.91 30.42 3.8816 0 2 1 4 24.02 11.45 3.7053 1 0 1 4 25.47 7.96 3.4971 1 2 0 4 25.55 68.74 3.4869 1 1 1 8 29.70 6.28 3.0085 1 2 1 8 30.29 56.36 2.9503 0 0 2 2 32.13 15.97 2.7861 1 3 0 4 35.64 100.00 2.5194 1 3 1 8 36.89 28.58 2.4368 1 1 2 8 38.11 13.84 2.3614 0 4 1 4 38.82 7.21 2.3195 2 1 0 4 39.78 19.60 2.2662 1 4 0 4 39.98 26.09 2.2550 1 2 2 8 41.80 7.34 2.1611 2 2 0 4 41.85 13.88 2.1587 2 1 1 8 44.65 1.13 2.0293 2 2 1 8 44.74 1.27 2.0256 1 3 2 8 46.81 2.05 1.9408 0 4 2 4 49.18 14.73 1.8527 2 0 2 4 50.68 7.23 1.8014 1 5 1 8 51.01 10.54 1.7902 1 1 3 8 52.32 11.26 1.7486 2 4 0 4 52.49 34.23 1.7434 2 2 2 8 53.33 3.23 1.7179 0 6 0 2 53.45 4.37 1.7143 1 2 3 8 54.75 15.35 1.6765 2 4 1 8 55.73 11.49 1.6494 0 6 1 4 57.34 22.40 1.6068 1 3 3 8 59.09 9.38 1.5635 0 4 3 4 61.10 1.62 1.5167 3 2 0 4 61.14 6.30 1.5159 3 1 1 8 61.55 3.73 1.5067 2 5 1 8 61.66 1.29 1.5042 2 4 2 8 61.85 2.64 1.5001 2 1 3 8 62.57 23.50 1.4845 0 6 2 4 63.01 15.52 1.4751 0 0 4 2 63.31 2.21 1.4690 3 2 1 8 66.46 6.88 1.4067 1 7 0 4 66.84 10.82 1.3996 3 3 1 8 67.04 2.72 1.3961 1 1 4 8 67.20 4.13 1.3930 2 6 0 4 68.86 1.76 1.3634 1 5 3 8 69.31 1.39 1.3558 2 6 1 8 69.57 4.43 1.3513 3 4 0 4 69.71 12.43 1.3489 3 2 2 8 71.64 3.35 1.3172 3 4 1 8 72.30 2.00 1.3068 2 4 3 8 72.50 1.88 1.3037 1 3 4 8 73.09 2.32 1.2946 3 3 2 8 73.14 4.22 1.2939 0 6 3 4 74.77 7.63 1.2698 1 7 2 8 75.88 1.06 1.2539 2 0 4 4 76.26 1.11 1.2486 1 6 3 8 76.54 1.10 1.2447 2 1 4 8 77.15 1.12 1.2363 1 4 4 8 77.24 1.58 1.2351 3 0 3 4 77.90 1.56 1.2263 3 1 3 8 78.27 2.20 1.2214 2 5 3 8 78.51 2.24 1.2184 2 2 4 8 80.73 2.68 1.1903 4 0 0 2 83.10 5.20 1.1623 3 3 3 8 83.32 1.39 1.1597 4 2 0 4 83.58 1.64 1.1568 3 5 2 8 83.95 1.70 1.1527 2 7 2 8 84.16 1.24 1.1503 0 2 5 4 84.55 1.19 1.1460 1 8 2 8 84.77 1.96 1.1436 3 6 1 8 85.25 1.16 1.1384 1 1 5 8 86.27 2.82 1.1275 2 4 4 8 87.08 2.33 1.1192 0 6 4 4 87.60 2.93 1.1138 3 4 3 8 87.63 1.10 1.1135 1 9 0 4 87.70 1.52 1.1128 2 8 1 8 89.24 2.51 1.0976 4 1 2 8 89.59 1.91 1.0942 1 9 1 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.