LiScSiO4 Hazen R M, Downs R T, Finger L W American Mineralogist 81 (1996) 327-334 High-pressure crystal chemistry of LiScSiO4: An olivine with nearly isotropic compression Sample: #2, P = 5.15 GPa _database_code_amcsd 0001787 CELL PARAMETERS: 4.7535 10.2864 5.8895 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 287.975 Density (g/cm3): 3.320 MAX. ABS. INTENSITY / VOLUME**2: 11.97324704 RIR: 1.174 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.24 23.24 5.1432 0 2 0 2 20.58 54.43 4.3150 1 1 0 4 22.96 29.71 3.8739 0 2 1 4 24.06 11.43 3.6990 1 0 1 4 25.52 8.15 3.4909 1 2 0 4 25.59 67.59 3.4808 1 1 1 8 29.75 6.43 3.0030 1 2 1 8 30.35 55.94 2.9448 0 0 2 2 32.19 15.51 2.7808 1 3 0 4 35.71 100.00 2.5146 1 3 1 8 36.96 28.51 2.4323 1 1 2 8 38.19 13.88 2.3567 0 4 1 4 38.89 7.05 2.3157 2 1 0 4 39.86 19.57 2.2618 1 4 0 4 40.06 25.74 2.2509 1 2 2 8 41.87 7.53 2.1575 2 2 0 4 41.92 13.29 2.1551 2 1 1 8 44.73 1.16 2.0259 2 2 1 8 44.83 1.31 2.0218 1 3 2 8 46.91 2.13 1.9370 0 4 2 4 49.27 14.22 1.8495 2 0 2 4 50.11 1.06 1.8203 2 1 2 8 50.78 7.06 1.7979 1 5 1 8 51.12 10.30 1.7869 1 1 3 8 52.42 11.40 1.7454 2 4 0 4 52.59 34.24 1.7404 2 2 2 8 53.45 3.35 1.7144 0 6 0 2 53.56 4.39 1.7111 1 2 3 8 54.86 14.93 1.6735 2 4 1 8 55.85 11.12 1.6461 0 6 1 4 57.46 22.36 1.6038 1 3 3 8 59.21 9.29 1.5604 0 4 3 4 61.21 1.67 1.5143 3 2 0 4 61.25 6.48 1.5134 3 1 1 8 61.67 3.74 1.5039 2 5 1 8 61.79 1.31 1.5015 2 4 2 8 61.97 2.58 1.4975 2 1 3 8 62.71 23.61 1.4816 0 6 2 4 63.15 15.44 1.4724 0 0 4 2 63.43 2.34 1.4666 3 2 1 8 66.61 6.85 1.4039 1 7 0 4 66.97 10.11 1.3973 3 3 1 8 67.18 2.72 1.3935 1 1 4 8 67.35 3.96 1.3904 2 6 0 4 69.01 1.74 1.3608 1 5 3 8 69.46 1.34 1.3532 2 6 1 8 69.71 4.52 1.3490 3 4 0 4 69.85 12.71 1.3467 3 2 2 8 71.79 3.40 1.3149 3 4 1 8 72.46 1.95 1.3044 2 4 3 8 72.66 1.83 1.3012 1 3 4 8 73.24 2.17 1.2924 3 3 2 8 73.31 4.07 1.2913 0 6 3 4 74.94 7.64 1.2673 1 7 2 8 76.43 1.12 1.2462 1 6 3 8 76.70 1.11 1.2425 2 1 4 8 77.33 1.15 1.2340 1 4 4 8 77.40 1.53 1.2330 3 0 3 4 78.06 1.67 1.2242 3 1 3 8 78.44 2.18 1.2192 2 5 3 8 78.68 2.32 1.2162 2 2 4 8 80.89 2.65 1.1884 4 0 0 2 83.28 4.91 1.1603 3 3 3 8 83.49 1.38 1.1579 4 2 0 4 83.76 1.74 1.1548 3 5 2 8 84.14 1.63 1.1505 2 7 2 8 84.36 1.22 1.1482 0 2 5 4 84.76 1.20 1.1437 1 8 2 8 84.96 1.95 1.1416 3 6 1 8 85.44 1.16 1.1363 1 1 5 8 86.47 2.86 1.1254 2 4 4 8 87.29 2.41 1.1170 0 6 4 4 87.80 3.01 1.1118 3 4 3 8 87.85 1.10 1.1113 1 9 0 4 87.92 1.56 1.1106 2 8 1 8 89.43 2.61 1.0958 4 1 2 8 89.82 1.93 1.0920 1 9 1 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.