Katoite Lager G A, Von Dreele R B American Mineralogist 81 (1996) 1097-1104 Neutron powder diffraction study of hydrogarnet to 9.0 GPa P = 7.9 GPa _database_code_amcsd 0001831 CELL PARAMETERS: 12.0770 12.0770 12.0770 90.000 90.000 90.000 SPACE GROUP: Ia-3d X-RAY WAVELENGTH: 1.541838 Cell Volume: 1761.478 Density (g/cm3): 2.852 MAX. ABS. INTENSITY / VOLUME**2: 9.969513663 RIR: 1.138 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.99 82.74 4.9304 2 1 1 24 20.80 29.70 4.2699 2 2 0 12 27.64 49.29 3.2277 3 2 1 48 29.59 33.56 3.0192 4 0 0 6 33.17 75.56 2.7005 4 2 0 24 34.84 5.54 2.5748 3 3 2 24 36.45 17.40 2.4652 4 2 2 24 37.99 28.56 2.3685 4 3 1 48 40.93 97.26 2.2049 5 2 1 48 42.34 4.30 2.1349 4 4 0 12 46.34 46.34 1.9591 5 3 2 48 46.34 53.66 1.9591 6 1 1 24 47.62 4.55 1.9095 6 2 0 24 52.50 9.37 1.7432 4 4 4 8 53.66 3.33 1.7079 5 4 3 48 54.81 44.01 1.6748 6 4 0 24 55.95 8.23 1.6435 7 2 1 48 55.95 1.12 1.6435 6 3 3 24 55.95 15.00 1.6435 5 5 2 24 57.07 55.56 1.6139 6 4 2 48 60.35 11.70 1.5338 6 5 1 48 61.42 12.04 1.5096 8 0 0 6 63.52 1.85 1.4646 8 2 0 24 64.56 2.25 1.4435 6 5 3 48 65.59 2.57 1.4233 8 2 2 24 66.61 1.96 1.4039 7 4 3 48 69.63 15.02 1.3502 8 4 0 24 71.61 7.43 1.3177 8 4 2 48 72.59 4.38 1.3023 6 5 5 24 72.59 1.88 1.3023 9 2 1 48 73.57 8.14 1.2874 6 6 4 24 74.54 1.84 1.2730 7 5 4 48 74.54 1.49 1.2730 8 5 1 48 76.47 3.32 1.2456 7 6 3 48 76.47 4.21 1.2456 9 3 2 48 77.43 1.32 1.2326 8 4 4 24 78.38 2.98 1.2200 8 5 3 48 78.38 3.54 1.2200 9 4 1 48 80.28 3.63 1.1958 7 7 2 24 81.23 2.09 1.1842 10 2 0 24 84.06 1.44 1.1515 10 3 1 48 84.06 1.88 1.1515 9 5 2 48 84.06 8.57 1.1515 7 6 5 48 86.87 6.69 1.1213 10 4 0 24 86.87 7.43 1.1213 8 6 4 48 87.80 3.98 1.1118 9 6 1 48 87.80 1.04 1.1118 10 3 3 24 88.74 12.17 1.1025 10 4 2 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.