Katoite Lager G A, Von Dreele R B American Mineralogist 81 (1996) 1097-1104 Neutron powder diffraction study of hydrogarnet to 9.0 GPa P = 9.0 GPa _database_code_amcsd 0001832 CELL PARAMETERS: 12.0240 12.0240 12.0240 90.000 90.000 90.000 SPACE GROUP: Ia-3d X-RAY WAVELENGTH: 1.541838 Cell Volume: 1738.389 Density (g/cm3): 2.890 MAX. ABS. INTENSITY / VOLUME**2: 9.967709269 RIR: 1.123 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.07 88.74 4.9088 2 1 1 24 20.90 29.84 4.2511 2 2 0 12 27.76 49.97 3.2135 3 2 1 48 29.72 34.12 3.0060 4 0 0 6 33.32 74.74 2.6886 4 2 0 24 35.00 5.58 2.5635 3 3 2 24 36.61 15.29 2.4544 4 2 2 24 38.16 28.70 2.3581 4 3 1 48 41.12 98.67 2.1953 5 2 1 48 42.53 4.97 2.1256 4 4 0 12 46.56 53.64 1.9506 6 1 1 24 46.56 46.36 1.9506 5 3 2 48 47.84 4.10 1.9012 6 2 0 24 51.55 1.01 1.7728 6 3 1 48 52.74 10.26 1.7355 4 4 4 8 53.92 2.99 1.7005 5 4 3 48 55.08 44.84 1.6674 6 4 0 24 56.22 8.17 1.6363 7 2 1 48 56.22 1.12 1.6363 6 3 3 24 56.22 15.34 1.6363 5 5 2 24 57.34 51.81 1.6068 6 4 2 48 60.64 11.84 1.5270 6 5 1 48 61.72 11.72 1.5030 8 0 0 6 63.84 1.92 1.4581 8 2 0 24 64.88 2.22 1.4371 6 5 3 48 65.92 1.98 1.4170 8 2 2 24 66.95 1.92 1.3978 7 4 3 48 69.98 13.32 1.3443 8 4 0 24 71.98 7.39 1.3119 8 4 2 48 72.97 1.97 1.2966 9 2 1 48 72.97 4.44 1.2966 6 5 5 24 73.95 7.24 1.2818 6 6 4 24 74.93 1.49 1.2674 8 5 1 48 74.93 1.85 1.2674 7 5 4 48 76.87 3.15 1.2402 7 6 3 48 76.87 4.08 1.2402 9 3 2 48 78.80 3.41 1.2146 9 4 1 48 78.80 3.06 1.2146 8 5 3 48 80.71 3.43 1.1906 7 7 2 24 81.66 2.60 1.1791 10 2 0 24 84.51 2.02 1.1464 9 5 2 48 84.51 8.44 1.1464 7 6 5 48 84.51 1.49 1.1464 10 3 1 48 87.35 6.89 1.1164 10 4 0 24 87.35 7.39 1.1164 8 6 4 48 88.29 1.05 1.1069 10 3 3 24 88.29 4.03 1.1069 9 6 1 48 89.23 10.27 1.0976 10 4 2 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.