Stilbite-Ca Cruciani G, Artioli G, Gualtieri A, Stahl K, Hanson J C American Mineralogist 82 (1997) 729-739 Dehydration dynamics of stilbite using synchrotron X-ray powder diffraction Sample: at T = 441 K _database_code_amcsd 0001921 13.7200 17.6808 17.4461 90 90 90 Amma atom x y z occ Uiso Si1 .1383 .3289 .1327 .76 .036 Al1 .1383 .3289 .1327 .24 .036 Si1p .1372 .2897 .3782 .76 .036 Al1p .1372 .2897 .3782 .24 .036 Si3 .0493 .4084 .2760 .76 .036 Al3 .0493 .4084 .2760 .24 .036 Si4 .1359 .1864 .2336 .76 .036 Al4 .1359 .1864 .2336 .24 .036 Si5 0 .2935 0 .76 .036 Al5 0 .2935 0 .24 .036 Na1 .25 .315 .082 .06 .078 Ca1 .25 .315 .082 .11 .078 Na2 .205 0 .251 .04 .078 Ca2 .205 0 .251 .07 .078 Na4 .25 .5 .1119 .11 .078 Ca4 .25 .5 .1119 .19 .078 Na5 .25 .5 .422 .10 .078 Ca5 .25 .5 .422 .17 .078 O1 .0673 .3468 .0577 .052 O1p .0666 .2668 .4520 .052 O3 .1212 .2417 .1601 .052 O3p .1232 .2143 .3225 .052 O4 .1015 .3888 .1955 .052 O4p .1250 .3740 .3375 .052 O7 .25 .3635 .1153 .052 O7p .25 .2783 .4051 .052 O8 .0652 .1162 .2104 .052 O9 .0672 .5 .2979 .052 O10 .25 .1579 .2265 .052 Wat1 .142 0 .389 .49 .090 Wat2 .0443 0 .5851 .090 Wat3 .107 0 -.052 .58 .090