Apatite-(CaOH) Wilson R M, Elliot J C, Dowker S E P American Mineralogist 84 (1999) 1406-1414 Rietveld refinement of the crystallographic structure of human dental enamel apatites Sample: H6L, synthetic _database_code_amcsd 0002297 CELL PARAMETERS: 9.4081 9.4081 6.8887 90.000 90.000 120.000 SPACE GROUP: P6_3/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 528.046 Density (g/cm3): 3.159 MAX. ABS. INTENSITY / VOLUME**2: 14.37523485 RIR: 1.482 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 10.86 10.42 8.1477 1 0 0 6 16.85 3.48 5.2605 1 0 1 12 18.86 2.29 4.7041 1 1 0 6 21.82 5.97 4.0738 2 0 0 6 22.89 8.58 3.8847 1 1 1 12 25.40 1.49 3.5065 2 0 1 12 25.87 34.81 3.4444 0 0 2 2 28.13 7.58 3.1725 1 0 2 12 28.99 16.10 3.0795 2 1 0 6 31.83 29.75 2.8114 1 2 1 12 31.83 70.25 2.8114 2 1 1 12 32.21 49.44 2.7790 1 1 2 12 32.98 61.02 2.7159 3 0 0 6 34.09 21.19 2.6302 2 0 2 12 35.53 3.91 2.5266 3 0 1 12 39.24 2.90 2.2957 2 1 2 12 39.24 1.28 2.2957 1 2 2 12 39.89 18.07 2.2598 1 3 0 6 39.89 4.95 2.2598 3 1 0 6 40.53 2.46 2.2259 2 2 1 12 42.08 4.05 2.1472 1 3 1 12 42.08 2.35 2.1472 3 1 1 12 42.38 1.42 2.1327 3 0 2 12 43.88 4.07 2.0635 1 1 3 12 44.48 1.04 2.0369 4 0 0 6 45.34 3.80 2.0004 2 0 3 12 46.77 29.67 1.9424 2 2 2 12 48.16 6.78 1.8894 1 3 2 12 48.16 4.33 1.8894 3 1 2 12 48.72 3.63 1.8692 2 3 0 6 49.52 9.11 1.8408 1 2 3 12 49.52 24.59 1.8408 2 1 3 12 50.60 6.95 1.8040 2 3 1 12 50.60 8.75 1.8040 3 2 1 12 51.39 6.50 1.7780 1 4 0 6 51.39 4.76 1.7780 4 1 0 6 52.16 1.20 1.7535 3 0 3 12 52.17 10.59 1.7533 4 0 2 12 53.19 14.10 1.7222 0 0 4 2 54.46 1.24 1.6849 1 0 4 12 55.97 5.95 1.6429 3 2 2 12 57.19 1.44 1.6106 1 3 3 12 57.19 2.18 1.6106 3 1 3 12 58.18 2.01 1.5858 5 0 1 12 58.90 1.08 1.5680 3 3 0 6 60.09 4.71 1.5398 2 4 0 6 60.56 3.43 1.5289 3 3 1 12 61.71 1.85 1.5031 2 1 4 12 61.71 2.94 1.5031 1 2 4 12 61.73 2.05 1.5027 2 4 1 12 63.12 8.74 1.4730 5 0 2 12 63.58 1.08 1.4634 5 1 0 6 64.02 6.52 1.4544 3 0 4 12 64.25 5.50 1.4496 3 2 3 12 65.17 6.53 1.4314 5 1 1 12 66.51 1.11 1.4058 1 4 3 12 69.83 1.46 1.3468 1 5 2 12 69.83 1.02 1.3468 5 1 2 12 71.79 4.39 1.3148 4 3 1 12 72.44 2.34 1.3047 5 2 0 6 73.94 1.35 1.2819 5 2 1 12 74.14 3.75 1.2789 2 4 3 12 74.99 1.06 1.2666 2 3 4 12 75.61 3.14 1.2576 2 1 5 12 75.61 1.46 1.2576 1 2 5 12 76.27 1.53 1.2484 3 4 2 12 76.70 1.20 1.2425 6 1 0 6 77.10 3.09 1.2370 1 4 4 12 77.10 1.44 1.2370 4 1 4 12 77.32 3.98 1.2341 5 1 3 12 78.38 5.35 1.2201 2 5 2 12 83.57 4.02 1.1570 4 3 3 12 84.36 1.55 1.1481 0 0 6 2 84.38 2.46 1.1479 2 4 4 12 84.38 1.53 1.1479 4 2 4 12 85.63 1.04 1.1344 5 2 3 12 87.45 4.20 1.1154 1 1 6 12 87.47 2.15 1.1151 5 1 4 12 88.07 1.30 1.1090 2 3 5 12 88.71 1.01 1.1027 5 3 2 12 88.71 1.09 1.1027 3 5 2 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.