Apatite-(CaOH) Wilson R M, Elliot J C, Dowker S E P American Mineralogist 84 (1999) 1406-1414 Rietveld refinement of the crystallographic structure of human dental enamel apatites Sample: RHP - enamel _database_code_amcsd 0002310 CELL PARAMETERS: 9.4586 9.4586 6.8809 90.000 90.000 120.000 SPACE GROUP: P6_3/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 533.126 Density (g/cm3): 3.020 MAX. ABS. INTENSITY / VOLUME**2: 12.79717733 RIR: 1.380 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 10.80 3.68 8.1914 1 0 0 6 16.83 4.90 5.2687 1 0 1 12 21.70 1.78 4.0957 2 0 0 6 22.82 5.99 3.8975 1 1 1 12 25.31 1.30 3.5194 2 0 1 12 25.90 34.82 3.4404 0 0 2 2 28.13 9.68 3.1720 1 0 2 12 28.84 12.03 3.0961 2 1 0 6 31.69 70.22 2.8234 2 1 1 12 31.69 29.78 2.8234 1 2 1 12 32.17 46.30 2.7821 1 1 2 12 32.80 71.58 2.7305 3 0 0 6 34.03 25.82 2.6343 2 0 2 12 35.37 4.16 2.5379 3 0 1 12 38.05 1.11 2.3647 2 2 0 6 39.14 3.83 2.3014 2 1 2 12 39.67 20.45 2.2719 1 3 0 6 39.67 2.65 2.2719 3 1 0 6 41.87 5.11 2.1573 1 3 1 12 41.87 1.38 2.1573 3 1 1 12 42.26 1.19 2.1388 3 0 2 12 43.87 4.48 2.0637 1 1 3 12 44.23 1.50 2.0478 4 0 0 6 45.32 3.30 2.0012 2 0 3 12 46.61 27.65 1.9487 2 2 2 12 47.99 8.61 1.8958 1 3 2 12 47.99 6.47 1.8958 3 1 2 12 48.44 3.35 1.8792 2 3 0 6 49.45 24.21 1.8430 2 1 3 12 49.45 8.52 1.8430 1 2 3 12 50.33 6.62 1.8128 2 3 1 12 50.33 8.66 1.8128 3 2 1 12 51.10 7.77 1.7875 1 4 0 6 51.10 5.90 1.7875 4 1 0 6 51.96 11.81 1.7597 4 0 2 12 52.08 1.31 1.7562 3 0 3 12 53.25 13.54 1.7202 0 0 4 2 54.51 1.76 1.6835 1 0 4 12 55.74 6.75 1.6492 3 2 2 12 57.06 1.65 1.6141 1 3 3 12 57.06 2.82 1.6141 3 1 3 12 57.86 1.75 1.5937 5 0 1 12 58.16 1.09 1.5862 4 1 2 12 58.55 1.55 1.5764 3 3 0 6 59.74 4.09 1.5480 2 4 0 6 60.22 3.06 1.5366 3 3 1 12 61.39 2.10 1.5103 2 4 1 12 61.68 2.21 1.5037 2 1 4 12 61.68 3.17 1.5037 1 2 4 12 62.82 8.77 1.4791 5 0 2 12 63.97 6.31 1.4555 3 0 4 12 64.06 5.05 1.4536 3 2 3 12 64.80 7.03 1.4387 5 1 1 12 69.49 1.20 1.3527 1 5 2 12 71.37 4.00 1.3216 4 3 1 12 71.99 1.02 1.3117 2 5 0 6 71.99 3.21 1.3117 5 2 0 6 73.50 1.18 1.2885 5 2 1 12 73.86 3.79 1.2831 2 4 3 12 74.82 1.11 1.2690 6 0 2 12 74.83 1.36 1.2689 2 3 4 12 75.62 3.03 1.2575 2 1 5 12 75.62 1.50 1.2575 1 2 5 12 75.87 2.49 1.2540 3 4 2 12 76.92 1.29 1.2395 4 1 4 12 76.92 2.98 1.2395 1 4 4 12 77.00 4.24 1.2384 5 1 3 12 77.95 4.93 1.2256 2 5 2 12 83.19 3.65 1.1613 4 3 3 12 84.13 2.65 1.1507 2 4 4 12 84.13 1.79 1.1507 4 2 4 12 84.48 1.33 1.1468 0 0 6 2 87.18 2.40 1.1181 5 1 4 12 87.53 4.58 1.1145 1 1 6 12 87.95 1.15 1.1103 2 3 5 12 88.19 1.05 1.1079 3 5 2 12 88.19 1.48 1.1079 7 0 2 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.