Titanite Kunz M, Arlt T, Stolz J American Mineralogist 85 (2000) 1465-1473 In situ powder diffraction study of titanite (CaTiOSiO4) at high pressure and high temperature Sample #004 at P = 1.21 GPa, T = 670 K _database_code_amcsd 0002527 CELL PARAMETERS: 7.0442 8.7132 6.5476 90.000 113.705 90.000 SPACE GROUP: P2_1/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 367.968 Density (g/cm3): 3.538 MAX. ABS. INTENSITY / VOLUME**2: 16.35759948 RIR: 1.505 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.10 1.16 5.1841 1 1 0 4 17.96 25.50 4.9390 0 1 1 4 18.66 1.10 4.7544 -1 1 1 4 20.38 3.21 4.3566 0 2 0 2 27.57 100.00 3.2349 -2 1 1 4 27.66 3.91 3.2249 2 0 0 2 29.81 73.05 2.9976 0 0 2 2 31.54 6.31 2.8368 -2 0 2 2 34.31 62.17 2.6138 0 3 1 4 34.61 47.88 2.5920 2 2 0 4 37.85 3.75 2.3772 -2 2 2 4 38.04 4.47 2.3654 2 1 1 4 39.40 17.88 2.2869 1 3 1 4 39.80 8.86 2.2648 -3 1 1 4 40.43 3.60 2.2309 -2 3 1 4 41.45 2.00 2.1783 0 4 0 2 42.92 7.23 2.1071 -1 1 3 4 43.36 4.55 2.0869 1 2 2 4 43.84 2.25 2.0652 -3 2 1 4 43.87 9.63 2.0638 1 4 0 4 43.89 16.35 2.0630 -2 1 3 4 45.87 1.82 1.9781 -3 2 2 4 46.63 6.20 1.9478 0 1 3 4 46.74 1.18 1.9435 -1 2 3 4 48.52 1.23 1.8761 2 3 1 4 49.11 3.53 1.8550 2 0 2 2 50.56 9.49 1.8051 2 4 0 4 51.89 1.16 1.7622 0 4 2 4 52.53 6.99 1.7420 -4 0 2 2 52.62 1.55 1.7392 -1 3 3 4 52.77 1.85 1.7348 -3 2 3 4 53.00 10.62 1.7277 -2 4 2 4 53.45 3.11 1.7141 -2 3 3 4 53.63 2.18 1.7089 -4 1 1 4 53.66 2.11 1.7082 -4 1 2 4 53.71 15.88 1.7067 2 2 2 4 55.13 1.61 1.6658 -1 5 1 4 55.84 23.41 1.6463 0 3 3 4 57.12 3.39 1.6125 4 0 0 2 58.18 1.36 1.5855 4 1 0 4 59.29 10.23 1.5585 -2 5 1 4 60.55 5.41 1.5292 -2 2 4 4 61.91 5.86 1.4988 0 0 4 2 62.11 16.50 1.4944 -4 3 1 4 64.13 2.91 1.4522 0 6 0 2 64.91 4.93 1.4367 2 1 3 4 65.68 5.67 1.4215 2 5 1 4 65.85 6.90 1.4184 -4 0 4 2 66.17 2.83 1.4123 2 4 2 4 66.37 6.02 1.4085 -4 3 3 4 66.83 1.27 1.3999 -4 1 4 4 69.82 7.49 1.3471 -2 5 3 4 72.30 6.86 1.3069 0 6 2 4 72.31 2.95 1.3066 -2 4 4 4 73.12 1.31 1.2943 -2 1 5 4 74.34 6.83 1.2760 4 3 1 4 77.71 3.86 1.2288 4 0 2 2 78.74 1.42 1.2153 -3 6 2 4 84.48 1.81 1.1468 2 2 4 4 86.02 2.08 1.1302 -4 3 5 4 87.23 1.25 1.1176 2 5 3 4 87.44 1.32 1.1154 -4 -6 2 4 87.93 3.15 1.1104 2 7 1 4 88.15 4.18 1.1083 0 3 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.