Titanite Kunz M, Arlt T, Stolz J American Mineralogist 85 (2000) 1465-1473 In situ powder diffraction study of titanite (CaTiOSiO4) at high pressure and high temperature Sample #005 at P = 1.26 GPa, T = 648 K _database_code_amcsd 0002528 CELL PARAMETERS: 7.0391 8.7100 6.5433 90.000 113.686 90.000 SPACE GROUP: P2_1/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 367.379 Density (g/cm3): 3.544 MAX. ABS. INTENSITY / VOLUME**2: 15.05481845 RIR: 1.383 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.11 2.85 5.1815 1 1 0 4 17.97 26.80 4.9367 0 1 1 4 20.39 2.18 4.3550 0 2 0 2 25.59 2.62 3.4813 -2 0 1 2 25.80 1.33 3.4536 -1 2 1 4 27.59 100.00 3.2326 -2 1 1 4 27.68 5.15 3.2231 2 0 0 2 29.55 1.27 3.0227 2 1 0 4 29.82 79.27 2.9960 0 0 2 2 31.56 8.27 2.8345 -2 0 2 2 32.94 1.49 2.7193 -2 2 1 4 33.24 2.12 2.6954 -2 1 2 4 34.32 59.76 2.6128 0 3 1 4 34.62 51.66 2.5907 2 2 0 4 36.58 1.40 2.4565 2 0 1 2 37.87 4.27 2.3756 -2 2 2 4 38.06 4.26 2.3643 2 1 1 4 39.42 20.22 2.2860 1 3 1 4 39.83 11.45 2.2633 -3 1 1 4 40.46 3.46 2.2297 -2 3 1 4 41.47 1.16 2.1775 0 4 0 2 42.03 1.34 2.1498 -3 1 2 4 42.24 1.51 2.1396 2 2 1 4 42.61 2.75 2.1218 -2 0 3 2 42.95 7.71 2.1058 -1 1 3 4 43.37 1.06 2.0862 3 1 0 4 43.38 5.14 2.0861 1 2 2 4 43.87 1.67 2.0639 -3 2 1 4 43.89 10.16 2.0630 1 4 0 4 43.92 16.62 2.0615 -2 1 3 4 45.91 2.79 1.9767 -3 2 2 4 46.65 6.94 1.9468 0 1 3 4 46.77 1.79 1.9424 -1 2 3 4 49.14 3.73 1.8542 2 0 2 2 50.59 10.63 1.8043 2 4 0 4 52.58 7.48 1.7406 -4 0 2 2 52.65 2.29 1.7383 -1 3 3 4 52.81 1.70 1.7335 -3 2 3 4 53.03 12.04 1.7268 -2 4 2 4 53.49 2.61 1.7131 -2 3 3 4 53.67 2.49 1.7078 -4 1 1 4 53.70 1.72 1.7069 -4 1 2 4 53.73 17.51 1.7060 2 2 2 4 55.16 2.46 1.6652 -1 5 1 4 55.87 23.79 1.6456 0 3 3 4 57.16 3.41 1.6115 4 0 0 2 57.80 1.34 1.5953 -3 4 1 4 58.22 1.34 1.5846 4 1 0 4 59.32 12.04 1.5578 -2 5 1 4 60.38 1.43 1.5331 3 3 1 4 60.40 1.06 1.5325 -3 1 4 4 60.59 6.00 1.5282 -2 2 4 4 61.94 6.14 1.4980 0 0 4 2 62.15 15.08 1.4935 -4 3 1 4 62.18 1.08 1.4929 -4 3 2 4 62.72 1.31 1.4813 1 3 3 4 64.15 2.83 1.4517 0 6 0 2 64.94 4.78 1.4361 2 1 3 4 65.39 1.20 1.4272 -3 4 3 4 65.71 6.87 1.4210 2 5 1 4 65.91 7.67 1.4173 -4 0 4 2 66.20 3.34 1.4117 2 4 2 4 66.42 5.27 1.4076 -4 3 3 4 66.89 1.12 1.3989 -4 1 4 4 67.42 1.03 1.3891 -5 1 2 4 69.86 8.49 1.3464 -2 5 3 4 72.33 6.89 1.3064 0 6 2 4 72.36 2.90 1.3059 -2 4 4 4 74.38 6.33 1.2754 4 3 1 4 76.47 1.60 1.2457 -5 1 4 4 77.75 3.83 1.2283 4 0 2 2 78.79 1.52 1.2147 -3 6 2 4 84.52 1.89 1.1463 2 2 4 4 86.09 1.84 1.1294 -4 3 5 4 87.27 1.52 1.1172 2 5 3 4 87.98 3.18 1.1100 2 7 1 4 88.20 4.26 1.1078 0 3 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.