Titanite Kunz M, Arlt T, Stolz J American Mineralogist 85 (2000) 1465-1473 In situ powder diffraction study of titanite (CaTiOSiO4) at high pressure and high temperature Sample #012 at P = 2.87 GPa, T = 666 K _database_code_amcsd 0002535 CELL PARAMETERS: 6.9915 8.6881 6.5068 90.000 113.492 90.000 SPACE GROUP: A2/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 362.482 Density (g/cm3): 3.592 MAX. ABS. INTENSITY / VOLUME**2: 14.95707736 RIR: 1.356 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.03 20.57 4.9189 0 1 1 4 20.44 1.21 4.3440 0 2 0 2 26.21 1.42 3.4003 1 1 1 4 27.78 100.00 3.2117 -2 1 1 4 27.83 1.07 3.2060 2 0 0 2 29.95 87.51 2.9837 0 0 2 2 31.80 7.30 2.8141 -2 0 2 2 34.42 74.82 2.6054 0 3 1 4 34.78 42.56 2.5796 2 2 0 4 38.10 3.37 2.3618 -2 2 2 4 38.21 5.67 2.3551 2 1 1 4 39.54 25.93 2.2794 1 3 1 4 40.10 11.30 2.2489 -3 1 1 4 40.64 4.94 2.2199 -2 3 1 4 41.58 4.47 2.1720 0 4 0 2 43.18 9.23 2.0952 -1 1 3 4 43.53 5.67 2.0792 1 2 2 4 44.02 7.75 2.0572 1 4 0 4 44.21 20.80 2.0487 -2 1 3 4 46.85 8.50 1.9390 0 1 3 4 48.72 2.05 1.8690 2 3 1 4 49.32 2.74 1.8476 2 0 2 2 50.77 10.69 1.7982 2 4 0 4 51.95 2.38 1.7602 3 1 1 4 52.08 2.58 1.7560 0 4 2 4 52.90 1.12 1.7309 -1 3 3 4 52.98 14.92 1.7282 -4 0 2 2 53.28 14.40 1.7194 -2 4 2 4 53.78 2.00 1.7044 -2 3 3 4 53.93 19.21 1.7002 2 2 2 4 54.03 4.81 1.6972 -4 1 1 4 55.33 2.64 1.6603 -1 5 1 4 56.09 25.12 1.6396 0 3 3 4 57.49 5.93 1.6030 4 0 0 2 59.55 13.78 1.5525 -2 5 1 4 60.96 7.26 1.5199 -2 2 4 4 62.23 5.10 1.4919 0 0 4 2 62.52 16.80 1.4855 -4 3 1 4 62.96 2.75 1.4764 1 3 3 4 64.34 1.57 1.4480 0 6 0 2 65.19 4.85 1.4311 2 1 3 4 65.94 8.99 1.4167 2 5 1 4 66.43 1.86 1.4073 2 4 2 4 66.45 13.09 1.4071 -4 0 4 2 66.89 7.92 1.3988 -4 3 3 4 70.19 7.91 1.3409 -2 5 3 4 71.32 2.21 1.3223 -1 6 2 4 72.57 5.91 1.3027 0 6 2 4 72.75 2.70 1.2998 -2 4 4 4 74.74 8.36 1.2702 4 3 1 4 76.94 1.45 1.2392 -5 3 1 4 78.08 1.47 1.2240 -5 3 3 4 78.12 3.96 1.2234 4 0 2 2 79.16 1.68 1.2099 -3 6 2 4 81.25 1.28 1.1841 2 0 4 2 82.24 1.60 1.1723 -3 3 5 4 84.88 2.39 1.1424 2 2 4 4 86.76 3.57 1.1225 -4 3 5 4 87.61 1.62 1.1137 2 5 3 4 87.99 1.48 1.1099 -4 -6 2 4 88.29 2.54 1.1069 2 7 1 4 88.64 4.76 1.1035 0 3 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.