Titanite Kunz M, Arlt T, Stolz J American Mineralogist 85 (2000) 1465-1473 In situ powder diffraction study of titanite (CaTiOSiO4) at high pressure and high temperature Sample #016 at P = 2.88 GPa, T = 371 K _database_code_amcsd 0002539 CELL PARAMETERS: 6.9786 8.6726 6.4910 90.000 113.491 90.000 SPACE GROUP: A2/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 360.294 Density (g/cm3): 3.613 MAX. ABS. INTENSITY / VOLUME**2: 14.62628428 RIR: 1.318 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.07 24.73 4.9080 0 1 1 4 20.48 2.28 4.3363 0 2 0 2 26.26 1.61 3.3933 1 1 1 4 27.83 100.00 3.2056 -2 1 1 4 27.88 1.33 3.2001 2 0 0 2 30.02 82.98 2.9765 0 0 2 2 31.87 7.56 2.8080 -2 0 2 2 34.49 81.59 2.6005 0 3 1 4 34.58 1.14 2.5940 -1 2 2 4 34.84 48.27 2.5749 2 2 0 4 38.18 3.20 2.3570 -2 2 2 4 38.29 5.44 2.3504 2 1 1 4 39.62 23.21 2.2750 1 3 1 4 40.17 12.39 2.2448 -3 1 1 4 40.72 7.21 2.2158 -2 3 1 4 41.66 4.45 2.1681 0 4 0 2 43.29 9.64 2.0902 -1 1 3 4 43.63 6.05 2.0747 1 2 2 4 44.10 8.61 2.0535 1 4 0 4 44.32 21.91 2.0440 -2 1 3 4 46.97 8.15 1.9344 0 1 3 4 48.82 2.15 1.8654 2 3 1 4 49.44 3.83 1.8436 2 0 2 2 50.87 9.25 1.7950 2 4 0 4 52.06 1.41 1.7568 3 1 1 4 52.19 2.60 1.7525 0 4 2 4 53.09 13.52 1.7250 -4 0 2 2 53.39 13.06 1.7161 -2 4 2 4 53.91 2.83 1.7007 -2 3 3 4 54.05 18.85 1.6966 2 2 2 4 54.14 4.64 1.6941 -4 1 1 4 55.15 1.17 1.6653 0 5 1 4 55.44 1.92 1.6573 -1 5 1 4 56.23 28.67 1.6360 0 3 3 4 57.61 6.30 1.6001 4 0 0 2 59.67 13.53 1.5497 -2 5 1 4 60.92 1.04 1.5207 3 4 0 4 61.12 7.55 1.5163 -2 2 4 4 61.80 1.19 1.5011 4 2 0 4 62.40 5.26 1.4883 0 0 4 2 62.65 19.41 1.4829 -4 3 1 4 63.11 1.54 1.4731 1 3 3 4 64.46 2.57 1.4454 0 6 0 2 65.35 5.34 1.4279 2 1 3 4 66.07 7.74 1.4141 2 5 1 4 66.58 1.85 1.4045 2 4 2 4 66.61 13.47 1.4040 -4 0 4 2 67.04 8.75 1.3960 -4 3 3 4 70.35 7.77 1.3382 -2 5 3 4 71.48 2.13 1.3198 -1 6 2 4 72.73 7.75 1.3002 0 6 2 4 72.94 2.49 1.2970 -2 4 4 4 74.90 9.18 1.2678 4 3 1 4 78.26 1.36 1.2216 -5 3 3 4 78.31 4.34 1.2209 4 0 2 2 79.34 1.62 1.2077 -3 6 2 4 81.47 1.09 1.1814 2 0 4 2 82.46 1.33 1.1696 -3 3 5 4 85.12 2.12 1.1398 2 2 4 4 87.00 3.79 1.1200 -4 3 5 4 87.84 1.36 1.1114 2 5 3 4 88.19 2.00 1.1079 -4 -6 2 4 88.49 2.83 1.1049 2 7 1 4 88.90 5.28 1.1009 0 3 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.