Titanite Kunz M, Arlt T, Stolz J American Mineralogist 85 (2000) 1465-1473 In situ powder diffraction study of titanite (CaTiOSiO4) at high pressure and high temperature Sample #017 at P = 2.66 GPa, T = 303 K _database_code_amcsd 0002540 CELL PARAMETERS: 6.9820 8.6748 6.4924 90.000 113.498 90.000 SPACE GROUP: P2_1/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 360.619 Density (g/cm3): 3.610 MAX. ABS. INTENSITY / VOLUME**2: 13.77153007 RIR: 1.242 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.21 1.33 5.1516 1 1 0 4 18.07 24.23 4.9090 0 1 1 4 20.48 2.89 4.3374 0 2 0 2 25.95 3.79 3.4333 -1 2 1 4 26.26 1.12 3.3941 1 1 1 4 27.82 100.00 3.2070 -2 1 1 4 30.02 97.16 2.9770 0 0 2 2 31.86 7.32 2.8091 -2 0 2 2 33.53 1.80 2.6724 -2 1 2 4 34.02 1.31 2.6353 1 3 0 4 34.48 79.85 2.6011 0 3 1 4 34.57 1.24 2.5946 -1 2 2 4 34.83 46.89 2.5758 2 2 0 4 38.17 3.04 2.3578 -2 2 2 4 38.28 6.78 2.3512 2 1 1 4 39.60 21.50 2.2756 1 3 1 4 40.15 13.97 2.2458 -3 1 1 4 40.71 7.49 2.2166 -2 3 1 4 41.65 3.96 2.1687 0 4 0 2 42.41 1.72 2.1313 -3 1 2 4 43.28 8.48 2.0906 -1 1 3 4 43.62 5.70 2.0752 1 2 2 4 44.09 8.92 2.0541 1 4 0 4 44.30 23.16 2.0445 -2 1 3 4 44.80 1.41 2.0232 -1 4 1 4 46.97 8.92 1.9347 0 1 3 4 47.11 1.65 1.9293 -1 2 3 4 47.48 1.00 1.9150 3 2 0 4 48.81 3.27 1.8660 2 3 1 4 49.42 3.08 1.8441 2 0 2 2 49.83 1.15 1.8298 1 3 2 4 50.85 9.39 1.7955 2 4 0 4 52.04 2.67 1.7574 3 1 1 4 52.18 1.98 1.7529 0 4 2 4 52.27 1.01 1.7502 -3 3 2 4 53.06 10.68 1.7258 -4 0 2 2 53.37 10.74 1.7166 -2 4 2 4 53.89 2.33 1.7012 -2 3 3 4 54.04 17.24 1.6971 2 2 2 4 54.11 4.90 1.6949 -4 1 1 4 54.82 1.74 1.6746 1 5 0 4 55.43 2.17 1.6577 -1 5 1 4 56.22 28.79 1.6363 0 3 3 4 57.39 1.73 1.6055 -4 2 1 4 57.58 5.71 1.6008 4 0 0 2 58.17 6.21 1.5859 -3 4 1 4 59.65 11.72 1.5501 -2 5 1 4 60.55 2.11 1.5292 -1 5 2 4 60.98 2.04 1.5194 -3 1 4 4 61.10 6.15 1.5167 -2 2 4 4 61.77 1.53 1.5017 4 2 0 4 62.00 1.01 1.4969 -4 2 3 4 62.39 6.04 1.4885 0 0 4 2 62.62 14.66 1.4835 -4 3 1 4 63.10 2.01 1.4734 1 3 3 4 64.45 2.46 1.4458 0 6 0 2 65.34 5.31 1.4282 2 1 3 4 65.90 2.08 1.4174 -3 4 3 4 66.05 6.73 1.4145 2 5 1 4 66.56 1.91 1.4049 2 4 2 4 66.58 10.17 1.4045 -4 0 4 2 67.01 6.94 1.3966 -4 3 3 4 67.78 2.02 1.3826 3 4 1 4 68.04 1.29 1.3779 -5 1 2 4 70.33 6.46 1.3385 -2 5 3 4 70.94 1.01 1.3285 -5 2 2 4 71.46 1.75 1.3202 -1 6 2 4 72.71 6.43 1.3005 0 6 2 4 72.92 2.95 1.2973 -2 4 4 4 74.87 7.09 1.2682 4 3 1 4 75.67 1.23 1.2569 -5 3 2 4 77.28 1.30 1.2346 -5 1 4 4 78.28 2.97 1.2213 4 0 2 2 81.45 1.17 1.1816 2 0 4 2 85.10 2.41 1.1401 2 2 4 4 86.96 2.92 1.1203 -4 3 5 4 87.81 1.22 1.1117 2 5 3 4 88.15 1.59 1.1083 -4 -6 2 4 88.46 1.95 1.1052 2 7 1 4 88.88 5.12 1.1011 0 3 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.