Titanite Kunz M, Arlt T, Stolz J American Mineralogist 85 (2000) 1465-1473 In situ powder diffraction study of titanite (CaTiOSiO4) at high pressure and high temperature Sample #024 at P = 3.86 GPa, T = 399 K _database_code_amcsd 0002547 CELL PARAMETERS: 6.9543 8.6586 6.4707 90.000 113.380 90.000 SPACE GROUP: A2/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 357.639 Density (g/cm3): 3.640 MAX. ABS. INTENSITY / VOLUME**2: 13.63235060 RIR: 1.219 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.11 27.90 4.8979 0 1 1 4 20.51 1.96 4.3293 0 2 0 2 24.85 1.77 3.5830 1 2 0 4 26.31 2.59 3.3872 1 1 1 4 27.93 100.00 3.1946 -2 1 1 4 27.96 1.01 3.1917 2 0 0 2 30.09 86.91 2.9697 0 0 2 2 32.00 8.20 2.7970 -2 0 2 2 34.55 97.35 2.5959 0 3 1 4 34.93 47.71 2.5690 2 2 0 4 38.31 3.72 2.3494 -2 2 2 4 38.37 5.88 2.3458 2 1 1 4 39.69 28.38 2.2712 1 3 1 4 40.31 12.60 2.2374 -3 1 1 4 40.83 9.89 2.2103 -2 3 1 4 41.73 5.37 2.1646 0 4 0 2 43.42 9.63 2.0842 -1 1 3 4 43.71 9.25 2.0710 1 2 2 4 44.18 6.77 2.0500 1 4 0 4 44.48 23.92 2.0369 -2 1 3 4 47.09 8.76 1.9300 0 1 3 4 47.62 1.76 1.9096 3 2 0 4 48.92 1.80 1.8620 2 3 1 4 49.53 4.30 1.8402 2 0 2 2 50.53 1.37 1.8064 -3 3 1 4 50.98 6.63 1.7915 2 4 0 4 52.17 1.18 1.7531 3 1 1 4 52.30 4.75 1.7493 0 4 2 4 53.16 1.03 1.7228 -1 3 3 4 53.31 14.66 1.7185 -4 0 2 2 53.53 13.52 1.7119 -2 4 2 4 54.08 3.12 1.6958 -2 3 3 4 54.16 19.78 1.6936 2 2 2 4 54.32 5.06 1.6888 -4 1 1 4 55.25 2.75 1.6625 0 5 1 4 55.55 2.82 1.6543 -1 5 1 4 56.35 30.34 1.6326 0 3 3 4 57.77 7.26 1.5958 4 0 0 2 59.80 11.61 1.5465 -2 5 1 4 61.07 1.36 1.5174 3 4 0 4 61.32 8.19 1.5117 -2 2 4 4 61.98 1.54 1.4973 4 2 0 4 62.56 5.26 1.4849 0 0 4 2 62.84 19.38 1.4787 -4 3 1 4 63.24 1.88 1.4704 1 3 3 4 64.58 2.50 1.4431 0 6 0 2 65.49 5.58 1.4253 2 1 3 4 66.20 7.58 1.4116 2 5 1 4 66.42 1.14 1.4076 1 6 0 4 66.58 1.16 1.4045 0 2 4 4 66.71 1.20 1.4021 2 4 2 4 66.90 14.42 1.3985 -4 0 4 2 67.30 9.82 1.3913 -4 3 3 4 69.89 1.76 1.3459 -4 4 2 4 70.55 6.05 1.3349 -2 5 3 4 71.26 1.11 1.3234 -5 2 2 4 71.64 3.19 1.3173 -1 6 2 4 72.87 8.70 1.2980 0 6 2 4 73.17 1.62 1.2935 -2 4 4 4 75.09 10.39 1.2651 4 3 1 4 78.50 4.70 1.2185 4 0 2 2 78.58 1.89 1.2174 -5 3 3 4 79.56 1.99 1.2049 -3 6 2 4 80.40 1.84 1.1943 3 6 0 4 81.65 1.09 1.1792 2 0 4 2 82.78 1.57 1.1659 -3 3 5 4 85.31 2.19 1.1377 2 2 4 4 87.37 4.38 1.1161 -4 3 5 4 88.47 2.27 1.1051 -4 -6 2 4 88.68 2.24 1.1030 2 7 1 4 89.14 5.93 1.0985 0 3 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.