Titanite Kunz M, Arlt T, Stolz J American Mineralogist 85 (2000) 1465-1473 In situ powder diffraction study of titanite (CaTiOSiO4) at high pressure and high temperature Sample #026 at P = 4.67 GPa, T = 658 K _database_code_amcsd 0002549 CELL PARAMETERS: 6.9496 8.6605 6.4654 90.000 113.342 90.000 SPACE GROUP: A2/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 357.285 Density (g/cm3): 3.644 MAX. ABS. INTENSITY / VOLUME**2: 14.11540136 RIR: 1.261 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.12 24.01 4.8964 0 1 1 4 26.32 1.76 3.3866 1 1 1 4 27.95 100.00 3.1925 -2 1 1 4 27.97 1.21 3.1904 2 0 0 2 30.11 82.07 2.9681 0 0 2 2 32.03 7.99 2.7943 -2 0 2 2 34.55 86.54 2.5961 0 3 1 4 34.69 1.42 2.5858 -1 2 2 4 34.93 50.49 2.5685 2 2 0 4 38.34 4.19 2.3479 -2 2 2 4 38.38 5.57 2.3454 2 1 1 4 39.68 28.34 2.2712 1 3 1 4 40.33 12.81 2.2361 -3 1 1 4 40.83 6.62 2.2099 -2 3 1 4 41.72 5.05 2.1651 0 4 0 2 43.45 10.45 2.0827 -1 1 3 4 43.72 6.22 2.0706 1 2 2 4 44.17 8.60 2.0503 1 4 0 4 44.52 22.11 2.0351 -2 1 3 4 47.11 8.59 1.9290 0 1 3 4 47.63 1.07 1.9091 3 2 0 4 48.92 1.62 1.8619 2 3 1 4 49.55 3.91 1.8398 2 0 2 2 50.54 1.04 1.8058 -3 3 1 4 50.97 8.93 1.7915 2 4 0 4 52.19 1.54 1.7527 3 1 1 4 52.30 2.98 1.7492 0 4 2 4 53.35 15.26 1.7172 -4 0 2 2 53.54 14.60 1.7115 -2 4 2 4 54.11 2.01 1.6949 -2 3 3 4 54.17 21.52 1.6933 2 2 2 4 54.35 5.13 1.6879 -4 1 1 4 55.55 2.30 1.6545 -1 5 1 4 56.37 28.69 1.6321 0 3 3 4 57.80 6.59 1.5952 4 0 0 2 59.80 14.90 1.5465 -2 5 1 4 61.37 9.44 1.5106 -2 2 4 4 62.00 1.06 1.4969 4 2 0 4 62.59 4.94 1.4841 0 0 4 2 62.87 17.98 1.4782 -4 3 1 4 63.26 1.84 1.4701 1 3 3 4 64.56 1.72 1.4434 0 6 0 2 65.51 5.36 1.4249 2 1 3 4 66.20 9.36 1.4117 2 5 1 4 66.72 1.43 1.4020 2 4 2 4 66.98 13.78 1.3972 -4 0 4 2 67.35 8.67 1.3903 -4 3 3 4 69.92 1.30 1.3454 -4 4 2 4 70.57 7.66 1.3346 -2 5 3 4 71.63 2.55 1.3174 -1 6 2 4 72.87 7.06 1.2981 0 6 2 4 73.21 1.91 1.2929 -2 4 4 4 75.10 9.13 1.2649 4 3 1 4 77.40 1.15 1.2330 -5 3 1 4 78.52 4.65 1.2182 4 0 2 2 78.64 1.66 1.2166 -5 3 3 4 79.57 1.51 1.2047 -3 6 2 4 80.40 1.12 1.1944 3 6 0 4 81.69 1.02 1.1788 2 0 4 2 82.86 1.60 1.1651 -3 3 5 4 85.34 2.13 1.1374 2 2 4 4 87.46 4.13 1.1153 -4 3 5 4 88.04 1.68 1.1094 2 5 3 4 88.49 1.75 1.1049 -4 -6 2 4 88.67 2.69 1.1031 2 7 1 4 89.19 5.16 1.0980 0 3 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.