Titanite Kunz M, Arlt T, Stolz J American Mineralogist 85 (2000) 1465-1473 In situ powder diffraction study of titanite (CaTiOSiO4) at high pressure and high temperature Sample #029 at P = 4.80 GPa, T = 522 K _database_code_amcsd 0002552 CELL PARAMETERS: 6.9409 8.6532 6.4551 90.000 113.331 90.000 SPACE GROUP: A2/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 355.998 Density (g/cm3): 3.657 MAX. ABS. INTENSITY / VOLUME**2: 14.91904041 RIR: 1.328 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.14 22.51 4.8901 0 1 1 4 20.53 1.81 4.3266 0 2 0 2 26.35 2.22 3.3825 1 1 1 4 27.98 100.00 3.1886 -2 1 1 4 28.00 1.89 3.1867 2 0 0 2 30.16 76.30 2.9636 0 0 2 2 32.08 7.46 2.7901 -2 0 2 2 34.58 84.45 2.5936 0 3 1 4 34.97 45.63 2.5658 2 2 0 4 38.39 3.34 2.3448 -2 2 2 4 38.43 5.32 2.3426 2 1 1 4 39.73 28.04 2.2689 1 3 1 4 40.39 11.53 2.2334 -3 1 1 4 40.88 7.17 2.2076 -2 3 1 4 41.75 3.97 2.1633 0 4 0 2 43.52 9.55 2.0795 -1 1 3 4 43.77 6.91 2.0680 1 2 2 4 44.21 7.59 2.0485 1 4 0 4 44.59 20.89 2.0320 -2 1 3 4 47.19 7.65 1.9262 0 1 3 4 47.69 1.31 1.9070 3 2 0 4 48.97 1.36 1.8599 2 3 1 4 49.61 3.72 1.8374 2 0 2 2 50.60 1.13 1.8039 -3 3 1 4 51.03 8.17 1.7898 2 4 0 4 52.25 1.06 1.7506 3 1 1 4 52.36 2.69 1.7473 0 4 2 4 53.26 1.27 1.7198 -1 3 3 4 53.43 14.19 1.7150 -4 0 2 2 53.61 14.22 1.7096 -2 4 2 4 54.19 2.34 1.6926 -2 3 3 4 54.24 19.47 1.6912 2 2 2 4 54.42 4.54 1.6859 -4 1 1 4 55.30 1.66 1.6613 0 5 1 4 55.60 2.35 1.6530 -1 5 1 4 56.45 27.90 1.6300 0 3 3 4 57.87 5.79 1.5933 4 0 0 2 59.86 11.59 1.5451 -2 5 1 4 60.98 1.39 1.5195 3 3 1 4 61.14 1.08 1.5158 3 4 0 4 61.48 8.31 1.5083 -2 2 4 4 62.08 1.22 1.4952 4 2 0 4 62.70 4.72 1.4818 0 0 4 2 62.95 17.83 1.4765 -4 3 1 4 63.35 1.82 1.4682 1 3 3 4 64.63 1.89 1.4422 0 6 0 2 65.60 5.11 1.4231 2 1 3 4 66.27 7.26 1.4103 2 5 1 4 66.47 1.16 1.4066 1 6 0 4 66.72 1.08 1.4019 0 2 4 4 66.80 1.47 1.4004 2 4 2 4 67.09 13.08 1.3950 -4 0 4 2 67.45 8.42 1.3885 -4 3 3 4 70.01 1.02 1.3439 -4 4 2 4 70.66 6.34 1.3331 -2 5 3 4 71.71 3.10 1.3161 -1 6 2 4 72.95 7.14 1.2968 0 6 2 4 73.32 1.86 1.2912 -2 4 4 4 75.20 9.00 1.2635 4 3 1 4 77.51 1.15 1.2316 -5 3 1 4 78.63 4.68 1.2167 4 0 2 2 78.76 1.60 1.2151 -5 3 3 4 79.67 2.01 1.2035 -3 6 2 4 80.49 1.51 1.1932 3 6 0 4 83.00 1.69 1.1634 -3 3 5 4 85.48 1.75 1.1359 2 2 4 4 87.62 3.94 1.1136 -4 3 5 4 88.16 1.22 1.1082 2 5 3 4 88.60 1.74 1.1038 -4 -6 2 4 88.77 2.87 1.1021 2 7 1 4 89.35 5.07 1.0965 0 3 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.