Clinopyroxene Hattori T, Nagai T, Yamanaka T, Werner S, Schulz H American Mineralogist 85 (2000) 1485-1491 Single-crystal X-ray diffraction study of FeGeO3 high-P clinopyroxene (C2/c) up to 8.2 GPa Sample at P = 8.2 GPa _database_code_amcsd 0002573 CELL PARAMETERS: 9.5830 8.8830 5.0930 90.000 100.560 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 426.203 Density (g/cm3): 5.500 MAX. ABS. INTENSITY / VOLUME**2: 27.14957456 RIR: 1.607 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.99 4.92 4.4415 0 2 0 2 21.03 3.57 4.2234 -1 1 1 4 23.81 2.41 3.7371 1 1 1 4 26.83 32.12 3.3226 0 2 1 4 27.60 34.32 3.2315 2 2 0 4 30.19 97.27 2.9607 3 1 0 4 30.99 90.61 2.8854 -2 2 1 4 31.68 1.61 2.8248 1 3 0 4 32.36 39.85 2.7665 -3 1 1 4 34.89 100.00 2.5717 2 2 1 4 35.62 98.12 2.5202 -1 3 1 4 35.87 71.17 2.5034 0 0 2 2 36.84 2.66 2.4400 -1 1 2 4 37.40 2.20 2.4043 1 3 1 4 37.47 1.76 2.4004 -2 0 2 2 37.88 13.25 2.3750 3 1 1 4 38.21 3.94 2.3552 4 0 0 2 40.24 7.39 2.2414 1 1 2 4 40.63 6.51 2.2208 0 4 0 2 42.82 4.36 2.1117 -2 2 2 4 43.10 30.89 2.0988 -3 1 2 4 43.60 4.86 2.0759 -3 3 1 4 43.96 2.26 2.0597 2 0 2 2 44.36 8.67 2.0422 -4 2 1 4 44.64 9.58 2.0300 0 4 1 4 45.14 12.52 2.0087 2 4 0 4 47.17 2.55 1.9268 -1 3 2 4 47.43 4.57 1.9167 -2 4 1 4 47.94 4.68 1.8977 -4 0 2 2 48.73 6.49 1.8685 2 2 2 4 49.45 7.83 1.8431 5 1 0 4 49.54 1.90 1.8399 -5 1 1 4 50.24 11.85 1.8159 2 4 1 4 51.73 7.43 1.7670 3 1 2 4 52.41 2.26 1.7458 1 5 0 4 55.08 1.07 1.6675 -1 1 3 4 55.30 4.69 1.6613 0 4 2 4 56.19 1.87 1.6371 5 1 1 4 56.44 3.89 1.6303 -5 1 2 4 56.45 1.71 1.6301 -2 4 2 4 58.02 1.47 1.5896 5 3 0 4 58.10 30.89 1.5875 -5 3 1 4 58.52 12.55 1.5772 4 0 2 2 58.62 6.44 1.5749 -3 1 3 4 58.81 7.24 1.5701 6 0 0 2 58.86 1.66 1.5689 1 1 3 4 59.01 6.92 1.5652 -2 2 3 4 59.14 1.06 1.5623 0 2 3 4 59.81 20.12 1.5463 3 5 0 4 61.39 6.55 1.5101 2 4 2 4 62.76 17.71 1.4805 0 6 0 2 63.13 34.53 1.4728 -1 3 3 4 63.96 15.42 1.4556 -6 0 2 2 64.15 38.13 1.4517 5 3 1 4 65.78 3.32 1.4197 0 6 1 4 65.82 5.65 1.4188 -4 2 3 4 66.17 12.04 1.4122 2 2 3 4 66.30 4.72 1.4097 1 5 2 4 66.64 1.49 1.4035 1 3 3 4 68.37 13.35 1.3721 -3 5 2 4 68.40 1.61 1.3715 5 1 2 4 69.76 1.36 1.3481 -7 1 1 4 70.60 1.74 1.3342 0 4 3 4 70.81 3.71 1.3306 7 1 0 4 73.23 1.29 1.2926 5 5 0 4 74.44 2.40 1.2746 -7 1 2 4 74.45 8.87 1.2743 0 6 2 4 74.83 1.64 1.2688 -2 0 4 2 75.06 5.83 1.2655 3 5 2 4 75.53 1.97 1.2587 -1 1 4 4 76.03 4.73 1.2517 -5 3 3 4 76.04 1.95 1.2517 0 0 4 2 76.77 1.01 1.2415 -4 4 3 4 77.10 2.38 1.2370 2 4 3 4 77.49 2.16 1.2318 7 1 1 4 77.49 3.82 1.2317 -3 1 4 4 78.63 1.23 1.2167 -6 2 3 4 79.87 2.30 1.2010 1 1 4 4 83.01 2.10 1.1633 -3 7 1 4 83.74 4.49 1.1550 -8 2 1 4 87.67 1.19 1.1131 -8 2 2 4 89.06 1.17 1.0993 -6 4 3 4 89.44 2.85 1.0956 7 1 2 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.