Franklinite Pavese A, Levy D, Hoser A American Mineralogist 85 (2000) 1497-1502 Cation distribution in synthetic zinc ferrite (Zn0.97Fe2.02O4) from in situ high temperature neutron powder diffraction Sample at T = 900 K _database_code_amcsd 0002581 CELL PARAMETERS: 8.4870 8.4870 8.4870 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 611.312 Density (g/cm3): 5.234 MAX. ABS. INTENSITY / VOLUME**2: 97.27649786 RIR: 6.051 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.10 4.98 4.9000 1 1 1 8 29.77 35.38 3.0006 2 2 0 12 35.07 100.00 2.5589 3 1 1 24 36.68 7.81 2.4500 2 2 2 8 42.61 13.61 2.1218 4 0 0 6 52.85 11.24 1.7324 4 2 2 24 56.33 26.08 1.6333 5 1 1 24 56.33 5.40 1.6333 3 3 3 8 61.84 35.81 1.5003 4 4 0 12 70.13 3.79 1.3419 6 2 0 24 73.12 7.84 1.2943 5 3 3 24 74.10 3.43 1.2795 6 2 2 24 78.00 1.35 1.2250 4 4 4 8 85.65 4.14 1.1341 6 4 2 48 88.49 6.65 1.1049 7 3 1 48 88.49 4.77 1.1049 5 5 3 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.