Franklinite Pavese A, Levy D, Hoser A American Mineralogist 85 (2000) 1497-1502 Cation distribution in synthetic zinc ferrite (Zn0.97Fe2.02O4) from in situ high temperature neutron powder diffraction Sample at T = 1000 K _database_code_amcsd 0002583 CELL PARAMETERS: 8.4956 8.4956 8.4956 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 613.172 Density (g/cm3): 5.218 MAX. ABS. INTENSITY / VOLUME**2: 95.23302000 RIR: 5.942 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.09 5.12 4.9049 1 1 1 8 29.74 35.50 3.0036 2 2 0 12 35.03 100.00 2.5615 3 1 1 24 36.64 7.55 2.4525 2 2 2 8 42.57 13.66 2.1239 4 0 0 6 52.79 11.13 1.7342 4 2 2 24 56.27 25.54 1.6350 5 1 1 24 56.27 5.25 1.6350 3 3 3 8 61.77 35.09 1.5018 4 4 0 12 70.05 3.70 1.3433 6 2 0 24 73.03 7.47 1.2956 5 3 3 24 74.02 2.99 1.2808 6 2 2 24 77.91 1.27 1.2262 4 4 4 8 85.54 4.00 1.1353 6 4 2 48 88.38 6.11 1.1060 7 3 1 48 88.38 4.46 1.1060 5 5 3 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.