Franklinite Pavese A, Levy D, Hoser A American Mineralogist 85 (2000) 1497-1502 Cation distribution in synthetic zinc ferrite (Zn0.97Fe2.02O4) from in situ high temperature neutron powder diffraction Sample at T = 1100 K _database_code_amcsd 0002584 CELL PARAMETERS: 8.5038 8.5038 8.5038 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 614.949 Density (g/cm3): 5.201 MAX. ABS. INTENSITY / VOLUME**2: 93.75121813 RIR: 5.870 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.07 5.29 4.9097 1 1 1 8 29.71 35.21 3.0065 2 2 0 12 35.00 100.00 2.5640 3 1 1 24 36.61 7.59 2.4548 2 2 2 8 42.52 13.77 2.1260 4 0 0 6 52.73 10.95 1.7358 4 2 2 24 56.21 24.99 1.6366 5 1 1 24 56.21 5.21 1.6366 3 3 3 8 61.70 34.45 1.5033 4 4 0 12 69.97 3.61 1.3446 6 2 0 24 72.95 7.24 1.2968 5 3 3 24 73.93 2.87 1.2820 6 2 2 24 77.82 1.23 1.2274 4 4 4 8 85.44 3.83 1.1364 6 4 2 48 88.27 5.86 1.1071 7 3 1 48 88.27 4.24 1.1071 5 5 3 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.