Franklinite Pavese A, Levy D, Hoser A American Mineralogist 85 (2000) 1497-1502 Cation distribution in synthetic zinc ferrite (Zn0.97Fe2.02O4) from in situ high temperature neutron powder diffraction Sample at T = 1200 K _database_code_amcsd 0002585 CELL PARAMETERS: 8.5130 8.5130 8.5130 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 616.947 Density (g/cm3): 5.186 MAX. ABS. INTENSITY / VOLUME**2: 92.23231242 RIR: 5.791 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.05 5.80 4.9150 1 1 1 8 29.68 34.41 3.0098 2 2 0 12 34.96 100.00 2.5668 3 1 1 24 36.56 7.95 2.4575 2 2 2 8 42.47 14.27 2.1282 4 0 0 6 52.67 10.44 1.7377 4 2 2 24 56.14 24.35 1.6383 5 1 1 24 56.14 5.17 1.6383 3 3 3 8 61.63 33.70 1.5049 4 4 0 12 69.88 3.36 1.3460 6 2 0 24 72.86 6.98 1.2982 5 3 3 24 73.84 2.96 1.2834 6 2 2 24 77.72 1.27 1.2287 4 4 4 8 85.32 3.45 1.1376 6 4 2 48 88.15 3.98 1.1083 5 5 3 24 88.15 5.60 1.1083 7 3 1 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.