Franklinite Pavese A, Levy D, Hoser A American Mineralogist 85 (2000) 1497-1502 Cation distribution in synthetic zinc ferrite (Zn0.97Fe2.02O4) from in situ high temperature neutron powder diffraction Sample at T = 1300 K _database_code_amcsd 0002586 CELL PARAMETERS: 8.5220 8.5220 8.5220 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 618.906 Density (g/cm3): 5.170 MAX. ABS. INTENSITY / VOLUME**2: 91.58595368 RIR: 5.768 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.03 5.80 4.9202 1 1 1 8 29.65 34.33 3.0130 2 2 0 12 34.92 100.00 2.5695 3 1 1 24 36.52 7.99 2.4601 2 2 2 8 42.43 13.98 2.1305 4 0 0 6 52.61 10.53 1.7395 4 2 2 24 56.08 23.99 1.6401 5 1 1 24 56.08 5.21 1.6401 3 3 3 8 61.56 33.13 1.5065 4 4 0 12 69.80 3.43 1.3474 6 2 0 24 72.77 6.90 1.2996 5 3 3 24 73.75 2.88 1.2847 6 2 2 24 77.62 1.15 1.2300 4 4 4 8 85.21 3.51 1.1388 6 4 2 48 88.03 5.57 1.1095 7 3 1 48 88.03 3.88 1.1095 5 5 3 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.