Franklinite Pavese A, Levy D, Hoser A American Mineralogist 85 (2000) 1497-1502 Cation distribution in synthetic zinc ferrite (Zn0.97Fe2.02O4) from in situ high temperature neutron powder diffraction Sample at T = 1400 K _database_code_amcsd 0002587 CELL PARAMETERS: 8.5318 8.5318 8.5318 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 621.044 Density (g/cm3): 5.152 MAX. ABS. INTENSITY / VOLUME**2: 90.16228992 RIR: 5.698 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.01 6.43 4.9258 1 1 1 8 29.61 33.68 3.0164 2 2 0 12 34.88 100.00 2.5724 3 1 1 24 36.48 8.35 2.4629 2 2 2 8 42.38 14.20 2.1330 4 0 0 6 52.55 10.25 1.7415 4 2 2 24 56.01 23.57 1.6419 5 1 1 24 56.01 5.17 1.6419 3 3 3 8 61.48 32.39 1.5082 4 4 0 12 69.71 3.32 1.3490 6 2 0 24 72.67 6.72 1.3011 5 3 3 24 73.65 2.93 1.2862 6 2 2 24 77.51 1.11 1.2315 4 4 4 8 85.09 3.36 1.1401 6 4 2 48 87.90 5.41 1.1107 7 3 1 48 87.90 3.70 1.1107 5 5 3 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.