Franklinite Pavese A, Levy D, Hoser A American Mineralogist 85 (2000) 1497-1502 Cation distribution in synthetic zinc ferrite (Zn0.97Fe2.02O4) from in situ high temperature neutron powder diffraction Sample at T = 1500 K _database_code_amcsd 0002588 CELL PARAMETERS: 8.5450 8.5450 8.5450 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 623.930 Density (g/cm3): 5.127 MAX. ABS. INTENSITY / VOLUME**2: 86.67344664 RIR: 5.504 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.98 6.63 4.9335 1 1 1 8 29.57 33.20 3.0211 2 2 0 12 34.82 100.00 2.5764 3 1 1 24 36.42 8.30 2.4667 2 2 2 8 42.31 14.74 2.1363 4 0 0 6 52.46 9.55 1.7442 4 2 2 24 55.91 22.09 1.6445 5 1 1 24 55.91 4.99 1.6445 3 3 3 8 61.37 30.83 1.5106 4 4 0 12 69.58 2.91 1.3511 6 2 0 24 72.54 6.05 1.3031 5 3 3 24 73.52 2.62 1.2882 6 2 2 24 77.37 1.13 1.2334 4 4 4 8 84.93 2.74 1.1419 6 4 2 48 87.73 3.15 1.1125 5 5 3 24 87.73 4.64 1.1125 7 3 1 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.