Cesanite Piotrowski A, Kahlenberg V, Fischer R X, Lee Y, Parise J B American Mineralogist 87 (2002) 715-720 The crystal structures of cesanite and its synthetic analogue - A comparison Sample: synthetic _database_code_amcsd 0002812 CELL PARAMETERS: 9.4434 9.4434 6.8855 90.000 90.000 120.000 SPACE GROUP: P-6 X-RAY WAVELENGTH: 1.541838 Cell Volume: 531.769 Density (g/cm3): 2.739 MAX. ABS. INTENSITY / VOLUME**2: 8.722810883 RIR: 1.037 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 10.82 22.07 8.1782 1 0 0 3 12.86 2.87 6.8855 0 0 1 2 16.83 8.27 5.2672 1 0 1 6 18.79 52.01 4.7217 1 1 0 3 21.73 1.92 4.0891 2 0 0 3 22.84 51.67 3.8941 1 1 1 6 25.33 2.65 3.5159 2 0 1 6 25.88 66.56 3.4427 0 0 2 2 28.88 1.39 3.0911 2 1 0 3 28.88 16.85 3.0911 1 2 0 3 31.73 27.83 2.8200 2 1 1 6 31.73 72.17 2.8200 1 2 1 6 32.18 57.85 2.7818 1 1 2 6 32.85 77.78 2.7261 3 0 0 3 34.04 23.62 2.6336 2 0 2 6 35.41 8.94 2.5347 3 0 1 6 38.12 1.34 2.3609 2 2 0 3 39.17 1.28 2.3000 2 1 2 6 39.17 3.60 2.3000 1 2 2 6 39.74 6.88 2.2682 1 3 0 3 39.74 19.97 2.2682 3 1 0 3 40.39 1.67 2.2332 2 2 1 6 41.94 1.70 2.1543 1 3 1 6 41.94 6.64 2.1543 3 1 1 6 43.86 1.49 2.0642 1 1 3 6 45.31 5.74 2.0014 2 0 3 6 46.32 1.38 1.9600 4 0 1 6 46.65 27.61 1.9470 2 2 2 6 48.03 1.47 1.8941 1 3 2 6 48.03 3.65 1.8941 3 1 2 6 48.52 3.44 1.8762 3 2 0 3 49.46 12.03 1.8427 2 1 3 6 49.46 25.42 1.8427 1 2 3 6 50.41 8.67 1.8102 2 3 1 6 50.41 6.98 1.8102 3 2 1 6 51.19 3.69 1.7846 4 1 0 3 52.02 5.18 1.7579 4 0 2 6 52.09 1.70 1.7557 3 0 3 6 53.01 1.78 1.7276 1 4 1 6 53.01 1.77 1.7276 4 1 1 6 53.21 13.74 1.7214 0 0 4 2 54.47 1.48 1.6845 1 0 4 6 55.80 5.34 1.6475 2 3 2 6 57.09 2.26 1.6133 1 3 3 6 57.09 2.67 1.6133 3 1 3 6 57.95 4.58 1.5914 5 0 1 6 58.23 1.66 1.5844 1 4 2 6 58.66 2.46 1.5739 3 3 0 3 59.84 6.05 1.5455 4 2 0 3 60.32 2.17 1.5343 3 3 1 6 61.49 4.01 1.5080 4 2 1 6 61.49 1.47 1.5080 2 4 1 6 61.68 1.94 1.5039 2 1 4 6 62.91 5.14 1.4774 5 0 2 6 63.32 1.28 1.4689 1 5 0 3 63.97 7.52 1.4555 3 0 4 6 64.11 6.94 1.4526 2 3 3 6 64.91 8.54 1.4365 1 5 1 6 66.29 1.61 1.4100 4 2 2 6 66.35 1.15 1.4089 1 4 3 6 66.35 1.99 1.4089 4 1 3 6 69.59 1.20 1.3510 1 5 2 6 69.59 1.00 1.3510 5 1 2 6 71.34 1.09 1.3220 1 1 5 6 71.50 5.34 1.3196 3 4 1 6 73.63 1.40 1.2865 2 5 1 6 73.93 1.03 1.2820 2 4 3 6 73.93 5.19 1.2820 4 2 3 6 75.59 1.29 1.2579 2 1 5 6 75.59 3.32 1.2579 1 2 5 6 76.36 1.22 1.2472 1 6 0 3 76.96 1.49 1.2390 4 1 4 6 77.09 4.94 1.2372 1 5 3 6 78.08 3.20 1.2240 5 2 2 6 78.08 1.14 1.2240 2 5 2 6 83.16 1.44 1.1616 3 3 4 6 83.29 4.24 1.1601 3 4 3 6 84.19 2.35 1.1500 4 2 4 6 84.41 1.95 1.1476 0 0 6 2 85.34 1.02 1.1374 2 5 3 6 87.25 1.77 1.1174 1 5 4 6 87.47 3.48 1.1151 1 1 6 6 87.96 1.09 1.1102 3 2 5 6 88.34 1.33 1.1063 5 3 2 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.