Pyroxene-ideal Thompson R M, Downs R T American Mineralogist 88 (2003) 653-666 Model pyroxenes I: Ideal pyroxene topologies Pyroxene #21b based on stacking sequence ABABCACBCBAC Note: Atoms Mg, Si, and O are assigned to atomic positions just for convenience. _database_code_amcsd 0003027 CELL PARAMETERS: 19.5959 6.0000 3.4641 90.000 90.000 90.000 SPACE GROUP: P2_1cn X-RAY WAVELENGTH: 1.541838 Cell Volume: 407.293 Density (g/cm3): 9.821 MAX. ABS. INTENSITY / VOLUME**2: 18.74827498 RIR: 0.622 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 20.10 1.16 4.4188 3 1 0 2 27.31 3.92 3.2660 6 0 0 1 29.78 8.32 3.0000 0 2 0 2 30.14 8.45 2.9654 1 1 1 4 31.18 13.01 2.8685 2 1 1 4 32.85 5.67 2.7262 3 1 1 4 35.07 1.03 2.5584 4 1 1 4 40.02 3.13 2.2528 1 2 1 4 40.84 27.48 2.2094 6 2 0 2 40.84 5.15 2.2094 6 1 1 4 40.84 8.98 2.2094 2 2 1 4 42.18 23.87 2.1423 3 2 1 4 44.00 35.10 2.0580 4 2 1 4 44.25 90.70 2.0467 9 1 0 2 44.25 9.30 2.0467 7 1 1 4 46.25 18.76 1.9629 5 2 1 4 47.95 4.20 1.8974 8 1 1 4 48.89 2.94 1.8628 6 2 1 4 51.89 7.37 1.7621 7 2 1 4 53.08 6.67 1.7253 1 3 1 4 53.08 3.34 1.7253 1 0 2 2 53.74 12.68 1.7056 2 3 1 4 53.74 6.34 1.7056 2 0 2 2 54.84 20.33 1.6742 3 3 1 4 54.84 10.16 1.6742 3 0 2 2 55.20 7.96 1.6641 8 2 1 4 55.41 1.12 1.6581 1 1 2 4 56.06 3.30 1.6406 10 1 1 4 56.06 3.35 1.6406 2 1 2 4 56.34 4.15 1.6330 12 0 0 1 56.34 24.81 1.6330 4 3 1 4 56.34 12.40 1.6330 4 0 2 2 57.12 9.15 1.6126 3 1 2 4 58.24 8.18 1.5842 5 3 1 4 58.24 4.09 1.5842 5 0 2 2 58.58 13.88 1.5757 4 1 2 4 58.79 1.43 1.5706 9 2 1 4 60.44 4.74 1.5317 11 1 1 4 60.44 7.77 1.5317 5 1 2 4 60.50 4.83 1.5302 6 3 1 4 60.50 2.42 1.5302 6 0 2 2 62.66 1.33 1.4827 6 1 2 4 62.66 1.45 1.4827 2 2 2 4 63.12 16.47 1.4729 7 3 1 4 63.12 8.23 1.4729 7 0 2 2 65.03 2.36 1.4343 12 1 1 4 65.22 3.42 1.4304 7 1 2 4 66.07 7.70 1.4142 8 3 1 4 66.07 3.85 1.4142 8 0 2 2 66.78 1.12 1.4009 11 2 1 4 68.12 3.91 1.3765 8 1 2 4 68.88 5.00 1.3631 6 4 0 2 68.88 1.79 1.3631 2 4 1 4 69.83 4.82 1.3469 3 4 1 4 71.15 1.78 1.3252 12 2 1 4 71.15 7.25 1.3252 4 4 1 4 71.33 1.94 1.3222 7 2 2 4 72.83 4.13 1.2987 5 4 1 4 72.89 6.10 1.2978 10 3 1 4 72.89 3.05 1.2978 10 0 2 2 74.30 2.44 1.2765 15 1 0 2 75.77 2.94 1.2554 13 2 1 4 76.75 2.77 1.2418 11 3 1 4 76.75 1.38 1.2418 11 0 2 2 77.23 1.95 1.2352 7 4 1 4 79.95 2.32 1.2000 8 4 1 4 80.67 2.05 1.1911 14 2 1 4 80.91 4.86 1.1882 12 3 1 4 80.91 2.43 1.1882 12 0 2 2 82.82 1.14 1.1655 12 1 2 4 84.42 1.63 1.1474 11 2 2 4 85.37 15.73 1.1371 13 3 1 4 85.37 7.87 1.1371 13 0 2 2 87.27 1.93 1.1172 13 1 2 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.