Boggsite Zanardi S, Cruciani G, Alberti A, Galli E American Mineralogist 89 (2004) 1033-1042 Dehydration and rehydration process in boggsite: an in-situ X-ray single-crystal study Note: Wat represents an unknown distribution across the Wat sites of [Ca.806,Mg.138,Na.041,K.007,Fe.006,Sr.001,Wat8.06] Note: Reported occupancies are discrepant with reported formula. Sample: BOG-RT, T = 25 C _database_code_amcsd 0003579 20.291 23.840 12.807 90 90 90 Imma atom x y z occ Uiso U(1,1) U(2,2) U(3,3) U(1,2) U(1,3) U(2,3) Al1 .18888 .18535 .6719 .24 .0252 .0267 .020 .0284 -.0007 .0024 -.0020 Si1 .18888 .18535 .6719 .76 .0252 .0267 .020 .0284 -.0007 .0024 -.0020 Al2 .19034 .02428 .3298 .33 .0276 .030 .0295 .0222 .0003 -.0020 -.0014 Si2 .19034 .02428 .3298 .67 .0276 .030 .0295 .0222 .0003 -.0020 -.0014 Al3 .07700 .18526 .8355 .26 .0250 .0264 .019 .0295 .0005 .0002 .0010 Si3 .07700 .18526 .8355 .74 .0250 .0264 .019 .0295 .0005 .0002 .0010 Al4 .07744 .02186 .1645 .26 .0257 .025 .0285 .0232 .0005 .0005 .0005 Si4 .07744 .02186 .1645 .74 .0257 .025 .0285 .0232 .0005 .0005 .0005 Al5 .22159 .08334 .5383 .07 .0257 .026 .024 .0262 -.0005 .0007 -.0032 Si5 .22159 .08334 .5383 .93 .0257 .026 .024 .0262 -.0005 .0007 -.0032 Al6 .12247 .08391 .9660 .05 .0250 .025 .023 .0262 -.0007 -.0000 .0047 Si6 .12247 .08391 .9660 .95 .0250 .025 .023 .0262 -.0007 -.0000 .0047 O1 .1887 .25 .6288 .039 .062 .019 .03577 .000 .00593 .000 O2 .1191 .1713 .7297 .044 .044 .041 .046 -.002 .010 -.004 O3 .1962 .1456 .5686 .044 .057 .032 .041 .006 .000 -.006 O4 .1897 .0703 .4254 .048 .065 .046 .033 .001 -.006 -.009 O5 .1183 .0321 .2727 .048 .038 .067 .038 -.000 -.006 -.006 O6 .0899 .25 .8737 .035 .042 .023 .03829 .000 -.00304 .000 O7 0 .1755 .8034 .043 .027 .044 .055 .000 0 -.010 O8 0 .0258 .1946 .048 .031 .070 .041 .000 0 .003 O9 .1960 .0388 .6221 .059 .099 .037 .039 -.005 .014 .008 O10 .0986 .1457 .9338 .048 .071 .029 .042 .002 -.005 .006 O11 .0950 .0721 .0820 .052 .073 .044 .037 -.004 .016 .009 O12 .2005 .0819 .9702 .078 .025 .099 .110 -.002 .000 .039 O13 .0952 .0385 .8859 .058 .096 .032 .045 -.005 -.016 -.010 O14 .25 .1752 .75 .051 .049 .048 .053 .000 -.019 .000 O15 .25 -.0395 .75 .054 .046 .071 .043 .000 -.005 .000 Wat1 0 .179 .108 .48 .144 Wat2 .190 .162 .207 .42 .101 Wat3 .194 .25 .045 .47 .110 Wat4 .110 .165 .403 .38 .131 Wat5 0 .164 .592 .36 .113 Wat6 0 .030 .410 .42 .137 Wat7 .071 .124 .402 .36 .109 Wat8 .050 .076 .619 .40 .140 Wat9 .153 .25 .235 .32 .057 Wat10 .130 .25 .082 .37 .144 Wat11 .208 .25 .405 .21 .125 Wat12 .197 .25 .233 .37 .091 Wat13 0 .086 .414 .24 .103