Tetranatrolite Lee Y, Hriljac J A, Vogt T American Mineralogist 90 (2005) 247-251 Variable-temperature structural studies of tetranatrolite from Mt. Saint-Hilaire: Synchrotron X-ray powder diffraction and Rietveld analysis Sample: at ambient conditions _database_code_amcsd 0003727 CELL PARAMETERS: 13.1988 13.1988 6.6288 90.000 90.000 90.000 SPACE GROUP: I-42d X-RAY WAVELENGTH: 1.541838 Cell Volume: 1154.792 Density (g/cm3): 2.334 MAX. ABS. INTENSITY / VOLUME**2: 8.307296052 RIR: 1.159 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.42 21.29 6.5994 2 0 0 4 14.96 58.25 5.9237 1 0 1 8 19.02 31.51 4.6665 2 2 0 4 20.14 44.66 4.4083 2 1 1 8 21.29 21.82 4.1738 3 1 0 8 27.02 2.96 3.2997 4 0 0 4 27.84 52.16 3.2045 3 2 1 8 28.58 19.72 3.1233 1 1 2 4 30.17 36.89 2.9618 2 0 2 8 30.28 3.69 2.9513 4 2 0 8 31.02 100.00 2.8826 4 1 1 8 34.56 15.21 2.5956 3 1 2 8 34.65 3.31 2.5885 5 1 0 8 36.64 19.92 2.4525 4 3 1 8 38.50 8.44 2.3384 4 0 2 8 38.59 6.90 2.3332 4 4 0 4 39.19 3.97 2.2988 5 2 1 8 39.74 9.02 2.2683 3 3 2 4 39.82 1.68 2.2636 5 3 0 8 40.95 24.15 2.2041 4 2 2 8 41.03 7.14 2.1998 6 0 0 4 43.36 1.57 2.0869 6 2 0 8 43.74 2.10 2.0694 2 1 3 8 45.96 4.37 1.9746 3 0 3 8 46.12 3.21 1.9683 5 4 1 8 48.10 7.42 1.8917 3 2 3 8 48.71 1.74 1.8692 5 3 2 8 49.82 12.18 1.8303 6 4 0 8 50.17 12.82 1.8185 4 1 3 8 50.31 5.64 1.8136 7 0 1 8 51.77 5.76 1.7660 6 2 2 8 52.31 3.64 1.7488 7 2 1 8 52.82 13.05 1.7331 7 3 0 8 54.13 4.28 1.6944 5 0 3 8 55.45 6.57 1.6572 0 0 4 2 55.71 1.53 1.6499 8 0 0 4 56.04 3.07 1.6411 5 2 3 8 56.17 9.21 1.6376 6 5 1 8 56.59 2.07 1.6264 7 1 2 8 56.59 6.53 1.6264 5 5 2 4 57.32 1.24 1.6073 2 0 4 8 57.59 2.01 1.6006 8 2 0 8 58.03 3.38 1.5894 8 1 1 8 58.03 1.45 1.5894 7 4 1 8 59.73 3.10 1.5482 6 1 3 8 60.07 3.94 1.5402 3 1 4 8 60.26 3.24 1.5358 7 3 2 8 61.52 2.61 1.5073 5 4 3 8 62.93 7.72 1.4770 8 0 2 8 62.99 4.61 1.4757 8 4 0 8 63.29 2.79 1.4694 6 3 3 8 64.49 1.99 1.4450 4 2 4 8 65.15 4.16 1.4319 9 0 1 8 66.74 1.14 1.4016 7 2 3 8 67.06 5.27 1.3957 5 1 4 8 67.24 2.95 1.3924 7 5 2 8 68.55 1.34 1.3689 8 5 1 8 69.58 3.40 1.3511 4 4 4 4 69.76 2.45 1.3481 8 4 2 8 70.10 2.22 1.3423 6 5 3 8 70.41 5.40 1.3372 5 3 4 8 70.59 1.14 1.3342 9 1 2 8 71.24 2.98 1.3236 6 0 4 8 71.48 1.47 1.3199 10 0 0 4 71.76 1.06 1.3154 7 4 3 8 71.76 4.92 1.3154 8 1 3 8 71.87 3.09 1.3136 9 4 1 8 73.88 2.40 1.2828 9 3 2 8 76.41 1.54 1.2465 3 2 5 8 77.91 1.48 1.2262 10 0 2 8 77.96 5.18 1.2255 10 4 0 8 78.01 3.27 1.2249 4 1 5 8 78.35 5.64 1.2204 8 7 1 8 80.13 7.09 1.1977 7 3 4 8 80.30 2.68 1.1957 9 5 2 8 81.53 1.04 1.1807 11 0 1 8 83.10 1.69 1.1622 11 2 1 8 84.57 3.38 1.1459 9 4 3 8 89.04 1.25 1.0995 6 3 5 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.