CaTiOSiO4 - CaTiOGeO4 join Ellemann-Olesen R, Malcherek T American Mineralogist 90 (2005) 1325-1334 A high-temperature diffraction study of the solid solution CaTiOSiO4 - CaTiOGeO4 Note: Titanite structure Sample: Single crystal CaTiOGeO4 _database_code_amcsd 0003881 CELL PARAMETERS: 7.1580 8.8850 6.6490 90.000 113.834 90.000 SPACE GROUP: P2_1/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 386.806 Density (g/cm3): 4.131 MAX. ABS. INTENSITY / VOLUME**2: 21.85203745 RIR: 1.723 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.67 2.45 5.0188 0 1 1 4 18.34 29.32 4.8375 -1 1 1 4 19.99 2.97 4.4425 0 2 0 2 24.21 13.12 3.6762 1 2 0 4 25.72 23.32 3.4643 1 1 1 4 27.11 100.00 3.2895 -2 1 1 4 27.24 16.02 3.2738 2 0 0 2 29.07 1.05 3.0719 2 1 0 4 29.37 94.74 3.0410 0 0 2 2 31.01 22.38 2.8836 -2 0 2 2 33.66 95.36 2.6627 0 3 1 4 33.72 12.19 2.6580 -1 2 2 4 34.02 62.85 2.6355 2 2 0 4 35.78 6.14 2.5094 0 2 2 4 37.17 12.07 2.4187 -2 2 2 4 37.47 8.22 2.4001 2 1 1 4 38.69 18.42 2.3271 1 3 1 4 39.67 19.72 2.2718 -2 3 1 4 40.62 1.98 2.2213 0 4 0 2 43.15 19.56 2.0965 -2 1 3 4 45.05 6.82 2.0122 -3 2 2 4 45.91 1.95 1.9765 0 1 3 4 46.35 1.41 1.9589 3 2 0 4 47.69 9.24 1.9072 2 3 1 4 48.39 9.30 1.8810 2 0 2 2 48.45 2.43 1.8789 -3 1 3 4 49.38 1.68 1.8457 -1 4 2 4 49.59 8.26 1.8381 2 4 0 4 51.62 18.60 1.7705 -4 0 2 2 51.69 1.70 1.7684 -1 3 3 4 51.96 8.52 1.7597 -2 4 2 4 52.47 9.24 1.7438 -2 3 3 4 52.85 21.98 1.7322 2 2 2 4 53.44 1.96 1.7145 1 1 3 4 54.88 35.35 1.6729 0 3 3 4 55.39 1.54 1.6586 -2 0 4 2 55.90 1.09 1.6447 -4 2 2 4 56.19 9.02 1.6369 4 0 0 2 58.08 22.31 1.5882 -2 5 1 4 59.37 5.00 1.5568 3 4 0 4 59.49 11.82 1.5539 -2 2 4 4 60.93 8.79 1.5205 0 0 4 2 60.97 23.57 1.5196 -4 3 1 4 61.63 1.32 1.5050 1 3 3 4 62.74 4.86 1.4808 0 6 0 2 63.89 5.90 1.4570 2 1 3 4 64.39 11.96 1.4470 2 5 1 4 64.52 1.00 1.4444 1 6 0 4 64.65 14.65 1.4418 -4 0 4 2 64.97 2.05 1.4355 2 4 2 4 65.09 10.74 1.4330 -4 3 3 4 65.36 1.25 1.4278 3 2 2 4 67.73 1.10 1.3835 -1 5 3 4 68.39 13.08 1.3716 -2 5 3 4 68.63 1.55 1.3676 -5 1 3 4 69.52 2.20 1.3522 -1 6 2 4 69.69 1.40 1.3492 2 6 0 4 70.47 2.30 1.3363 0 5 3 4 70.77 9.66 1.3314 0 6 2 4 70.91 2.35 1.3290 -2 4 4 4 71.72 2.21 1.3161 -1 4 4 4 71.82 1.66 1.3143 -2 1 5 4 72.46 1.26 1.3044 1 2 4 4 72.91 1.01 1.2975 -3 1 5 4 73.01 11.29 1.2959 4 3 1 4 74.94 1.03 1.2672 -5 3 1 4 75.86 2.02 1.2542 -4 5 1 4 75.88 1.11 1.2539 -5 3 3 4 76.42 5.48 1.2464 4 0 2 2 76.76 1.30 1.2417 3 1 3 4 77.02 1.79 1.2381 -3 6 2 4 78.96 1.65 1.2125 -2 3 5 4 79.52 2.11 1.2054 2 0 4 2 80.01 1.36 1.1992 -3 3 5 4 80.63 1.41 1.1915 -6 0 2 2 83.01 3.25 1.1634 2 2 4 4 84.11 2.24 1.1509 -6 -2 2 4 84.26 5.41 1.1492 -4 3 5 4 85.48 4.66 1.1359 -4 6 2 4 85.48 3.30 1.1359 2 5 3 4 85.93 1.52 1.1311 2 7 1 4 86.49 6.89 1.1252 0 3 5 4 87.06 1.31 1.1194 4 5 1 4 87.92 1.32 1.1106 0 8 0 2 89.18 4.18 1.0981 4 6 0 4 89.63 1.12 1.0938 -6 -2 4 4 89.89 1.73 1.0913 6 0 0 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.