CaTiOSiO4 - CaTiOGeO4 join Ellemann-Olesen R, Malcherek T American Mineralogist 90 (2005) 1325-1334 A high-temperature diffraction study of the solid solution CaTiOSiO4 - CaTiOGeO4 Note: Titanite structure Sample: #95, CaTiO(Ge.90Si.10)O4 _database_code_amcsd 0003882 CELL PARAMETERS: 7.1429 8.8782 6.6427 90.000 113.833 90.000 SPACE GROUP: P2_1/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 385.330 Density (g/cm3): 4.070 MAX. ABS. INTENSITY / VOLUME**2: 21.60741432 RIR: 1.729 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.69 2.11 5.0143 0 1 1 4 18.36 18.34 4.8314 -1 1 1 4 20.00 1.64 4.4391 0 2 0 2 24.24 10.78 3.6718 1 2 0 4 25.75 20.68 3.4596 1 1 1 4 27.16 100.00 3.2834 -2 1 1 4 27.30 13.01 3.2669 2 0 0 2 29.13 1.04 3.0659 2 1 0 4 29.40 86.78 3.0381 0 0 2 2 31.06 19.24 2.8794 -2 0 2 2 32.70 1.14 2.7389 -2 1 2 4 33.69 84.82 2.6606 0 3 1 4 33.75 10.39 2.6556 -1 2 2 4 34.07 56.06 2.6312 2 2 0 4 35.82 4.38 2.5072 0 2 2 4 37.22 8.82 2.4157 -2 2 2 4 37.54 7.55 2.3961 2 1 1 4 38.74 16.58 2.3247 1 3 1 4 39.73 16.16 2.2689 -2 3 1 4 40.65 1.95 2.2195 0 4 0 2 43.20 18.11 2.0942 -2 1 3 4 45.13 5.10 2.0090 -3 2 2 4 45.96 1.99 1.9747 0 1 3 4 46.44 1.15 1.9553 3 2 0 4 47.75 8.33 1.9046 2 3 1 4 48.47 7.50 1.8782 2 0 2 2 48.52 1.73 1.8762 -3 1 3 4 49.42 1.09 1.8441 -1 4 2 4 49.66 8.78 1.8359 2 4 0 4 51.74 17.29 1.7670 -4 0 2 2 51.74 1.03 1.7669 -1 3 3 4 52.02 7.90 1.7579 -2 4 2 4 52.53 7.10 1.7421 -2 3 3 4 52.84 1.39 1.7326 -4 1 1 4 52.93 19.65 1.7298 2 2 2 4 53.51 1.04 1.7126 1 1 3 4 54.93 31.43 1.6714 0 3 3 4 55.45 1.39 1.6570 -2 0 4 2 56.32 7.42 1.6334 4 0 0 2 58.14 18.97 1.5866 -2 5 1 4 59.46 3.56 1.5545 3 4 0 4 59.55 10.42 1.5524 -2 2 4 4 60.99 6.64 1.5191 0 0 4 2 61.09 20.11 1.5168 -4 3 1 4 61.70 1.15 1.5034 1 3 3 4 62.80 3.86 1.4797 0 6 0 2 63.98 4.68 1.4551 2 1 3 4 64.47 8.56 1.4454 2 5 1 4 64.75 12.72 1.4397 -4 0 4 2 65.05 1.78 1.4338 2 4 2 4 65.20 8.10 1.4308 -4 3 3 4 68.47 9.79 1.3704 -2 5 3 4 69.58 1.75 1.3511 -1 6 2 4 69.77 1.09 1.3479 2 6 0 4 70.53 1.81 1.3352 0 5 3 4 70.83 6.94 1.3303 0 6 2 4 70.99 2.25 1.3278 -2 4 4 4 71.79 1.42 1.3149 -1 4 4 4 71.90 1.17 1.3131 -2 1 5 4 73.15 8.84 1.2937 4 3 1 4 75.99 1.13 1.2523 -4 5 1 4 76.58 4.29 1.2442 4 0 2 2 77.12 1.50 1.2368 -3 6 2 4 79.05 1.11 1.2114 -2 3 5 4 79.63 1.51 1.2039 2 0 4 2 80.11 1.19 1.1980 -3 3 5 4 83.13 2.21 1.1620 2 2 4 4 84.38 4.21 1.1478 -4 3 5 4 85.60 2.35 1.1346 2 5 3 4 85.62 3.40 1.1345 -4 6 2 4 86.04 1.34 1.1300 2 7 1 4 86.59 4.89 1.1242 0 3 5 4 88.00 1.06 1.1098 0 8 0 2 89.33 3.16 1.0966 4 6 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.